Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
HDPE Marlex® 9708 Chevron Phillips Chemical Company LLC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Chevron Phillips Chemical Company LLC/Marlex® 9708 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,模压成型 | ASTM D256 | 40 J/m |
| hardness | Test Condition | Test Method | Chevron Phillips Chemical Company LLC/Marlex® 9708 |
|---|---|---|---|
| Shore hardness | 邵氏D,模压成型 | ASTM D2240 | 66 |
| Mechanical properties | Test Condition | Test Method | Chevron Phillips Chemical Company LLC/Marlex® 9708 |
|---|---|---|---|
| Flexural modulus | CompressionMolded，正切 | ASTM D790 | 1580 MPa |
| elongation | 断裂,模压成型 | ASTM D638 | 800 % |
| tensile strength | 屈服,模压成型 | ASTM D638 | 32.0 MPa |
| physical property | Test Condition | Test Method | Chevron Phillips Chemical Company LLC/Marlex® 9708 |
|---|---|---|---|
| density | ASTM D1505 | 0.962 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 8.0 g/10min |
| Environmental stress cracking resistance | 100%Igepal,模压成型,F50 | ASTM D1693B | <10.0 hr |
| Thermal performance | Test Condition | Test Method | Chevron Phillips Chemical Company LLC/Marlex® 9708 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,模压成型，HDT | ASTM D648 | 66.0 °C |
| vicat | ASTM D15255 | 127 °C | |
| Heat distortion temperature | 1.8MPa,未退火,模压成型，HDT | ASTM D648 | 49.0 °C |
| brittle temperature | ASTM D746A | <-75.0 °C |