ABS P2H-AT ABS vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

ABS ELIX POLYMERS SPANISH P2H-AT

Anti static level

US$ 2,480 / MT

FOB Dongguan Port

Electrical performance	Test Condition	Test Method	ELIX POLYMERS SPANISH/P2H-AT
Dissipation factor	23°C,1MHz	IEC 60250	9E-03
Dielectric strength	1.50mm	IEC 60243-1	32 KV/mm
Dissipation factor	100Hz	IEC 60250	5E-03
Dielectric strength	23°C,1.00mm	IEC 60243-1	34 KV/mm
Compared to the anti leakage trace index		IEC 60112	PLC 1
Volume resistivity		IEC 60093	1E+15 ohms·cm
Dissipation factor	1MHz	IEC 60250	6E-03
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Relative permittivity	100Hz	IEC 60250	2.90
Surface resistivity		IEC 60093	1E+15 ohms
Relative permittivity	23°C,100Hz	IEC 60250	3.00
Relative permittivity		1MHz	IEC 60250	3.10
Dissipation factor	23°C,100Hz	IEC 60250	5.5E-03
Relative permittivity	23°C,1MHz	IEC 60250	2.90
mechanical properties	Test Condition	Test Method	ELIX POLYMERS SPANISH/P2H-AT
Tensile creep modulus	1hr	ISO 899-1	2200 Mpa
bending strength		ISO 178	101 Mpa
tensile strength	Yield,23°C	ISO 527-2	74.0 Mpa
Tensile strain	Break,23°C	ISO 527-2/50	>15 %
bending strength	23°C	ISO 178	70.0 Mpa
tensile strength	Break,23°C	ISO 527-2	74.0 Mpa
Tensile modulus		ISO 527-2	5500 Mpa
tensile strength	Yield,23°C	ISO 527-2/50	44.0 Mpa
Bending modulus	23°C	ISO 178	2400 Mpa
Tensile modulus	23°C	ISO 527-2/1	2500 Mpa
Bending modulus		ISO 178	5400 Mpa
Tensile creep modulus	1000hr	ISO 899-1	1500 Mpa
Tensile strain	Break,23°C	ISO 527-2	2.0 %
Tensile strain		Yield,23°C	ISO 527-2/50	2.1 %
impact performance	Test Condition	Test Method	ELIX POLYMERS SPANISH/P2H-AT
Impact strength of simply supported beam without notch	-30°C	ISO 179	20 kJ/m²
		23°C	ISO 179/1eU	100 kJ/m²
		-30°C	ISO 179/1eU	80 kJ/m²
		23°C	ISO 179	18 kJ/m²
Physical properties	Test Condition	Test Method	ELIX POLYMERS SPANISH/P2H-AT
Shrinkage rate		ISO 294-4	0.20-0.40 %
Shrinkage rate		MD	ISO 294-4	0.40-0.60 %
ash content			16 %
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	3.00 cm3/10min
Shrinkage rate	TD	ISO 294-4	0.40-0.60 %
hardness	Test Condition	Test Method	ELIX POLYMERS SPANISH/P2H-AT
Ball Pressure Test		ISO 2039-1	110 Mpa
thermal performance	Test Condition	Test Method	ELIX POLYMERS SPANISH/P2H-AT
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	93.0 °C
Linear coefficient of thermal expansion	MD	ISO 11359-1	4E-05 cm/cm/°C
Linear coefficient of thermal expansion		MD：23to55°C	ISO 11359-2	9E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	97.0 °C
Vicat softening temperature		ISO 306/B50	98.0 °C
flammability	Test Condition	Test Method	ELIX POLYMERS SPANISH/P2H-AT
Burning wire flammability index	2.0mm	IEC 60695-2-12	700 °C
UL flame retardant rating	1.6mm	UL 94	HB
Burning rate	2.00mm	ISO 3795	60 mm/min