HMW-HDPE LUBMER™ LS4140 Mitsui Chemicals America, Inc.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | Mitsui Chemicals America, Inc./LUBMER™ LS4140 | |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 102 |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 175 °C |
| dielectric strength | ASTM D149 | 25 kV/mm | |
| dielectric constant | ASTM D150 | 3.20 | |
| elongation | 断裂,23°C | ASTM D638 | 150 % |
| Shrinkage rate | MD：2.00mm | ASTM D955 | 0.80 % |
| vicat | ASTM D15254 | 200 °C | |
| density | ASTM D792 | 1.10 g/cm³ | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 8E-05 cm/cm/°C |
| Dissipation Factor | 1MHz | ASTM D150 | 0.016 |
| Water absorption rate | 24hr | ASTM D570 | 1.5 % |
| Flexural modulus | 23°C,3.00mm,48.0mmSpan | ASTM D790 | 2200 MPa |
| Shrinkage rate | TD：2.00mm | ASTM D955 | 1.0 % |
| tensile strength | 断裂,23°C | ASTM D638 | 62.0 MPa |
| Impact strength of cantilever beam gap | 23°C,2.00mm | ASTM D256 | 88 J/m |
| tensile strength | 屈服,23°C | ASTM D638 | 60.0 MPa |
| bending strength | Yield,23°C,3.00mm,48.0mmSpan | ASTM D790 | 82.0 MPa |
| Volume resistivity | ASTM D257 | 1E+16 ohms·cm |