Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA610 QCL-4036 BK SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic and Electrical、Fitness equipment
Thermal stability、Conductive、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA610/SABIC INNOVATIVE US/QCL-4036 BK
Shrinkage rate
MD：24小时
ASTMD955
%
0
Shrinkage rate
TD：24hr
ASTMD955
%
0
Water absorption rate
24hr,50%RH
ASTMD570
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PA610/SABIC INNOVATIVE US/QCL-4036 BK
UnnotchedIzodImpactStrength
23°C
ISO180/1U
kJ/m²
5
Multi axis Instrumented Impact Energy
ISO6603-2
J
3
Tensile modulus
ASTMD638
Mpa
1
Tensile modulus
ISO527-2/1
Mpa
1
tensile strength
断裂
ASTMD638
Mpa
2
tensile strength
断裂
ISO527-2/5
Mpa
1
Wear factor
Washer
ASTMD3702Modified
10^-10in^5-min/ft-lb-hr
2
Wear factor
Ring
ASTMD3702Modified
10^-10in^5-min/ft-lb-hr
0
elongation
断裂
ASTMD638
%
2
elongation
断裂
ISO527-2/5
%
2
Bending modulus
50.0mm跨距
ASTMD790
Mpa
1
Bending modulus
ISO178
Mpa
1
bending strength
ISO178
Mpa
2
bending strength
屈服,50.0mm跨距
ASTMD790
Mpa
2
bending strength
断裂,50.0mm跨距
ASTMD790
Mpa
2
Suspended wall beam notch impact strength
23°C
ISO180/1A
kJ/m²
1
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
1
Thermal performance
Test Condition
Test Method
Unit
PA610/SABIC INNOVATIVE US/QCL-4036 BK
Hot deformation temperature
0.45MPa,Unannealed,64.0mmSpan
ISO75-2/Bf
°C
2
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
2
Linear coefficient of thermal expansion
MD：-30到30°C
ASTMD696
cm/cm/°C
2
Linear coefficient of thermal expansion
TD：-30to30°C
ASTMD696
cm/cm/°C
5