Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 1401X06 TORAY JAPAN
Toraycon®
Automotive sector、Shell
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/1401X06 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | ISO 179 | NoBreak |
| 23°C | ISO 179 | 240 kJ/m² |
| Supplementary Information | Test Condition | Test Method | TORAY JAPAN/1401X06 |
|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 103 mm |
| hardness | Test Condition | Test Method | TORAY JAPAN/1401X06 |
|---|---|---|---|
| Rockwell hardness | M计秤,23°C | ISO 2039-2 | 77 |
| Basic performance | Test Condition | Test Method | TORAY JAPAN/1401X06 |
|---|---|---|---|
| Water absorption rate | 23℃·24小时 | ASTM D-570 | 0.08 % |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/1401X06 |
|---|---|---|---|
| dielectric constant | ASTM D150/IEC 60250 | 3.3 | |
| Volume resistivity | ASTM D-257 | 4.0 cm×10 | |
| Dissipation Factor | 23°C,50Hz | IEC 60250 | 2E-03 |
| Volume resistivity | ASTM D257/IEC 60093 | 4.0*10^14 Ω.cm | |
| arc resistance | ASTM D-495 | 144 秒 | |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 0.020 |
| dielectric constant | 23°C,1kHz | IEC 60250 | 3.30 |
| 23°C,50Hz | IEC 60250 | 3.30 | |
| dielectric strength | IEC 60243-1 | 17 KV/mm | |
| arc resistance | IEC 60950 | 144 sec | |
| Volume resistivity | IEC 60093 | 8E+16 ohms·cm | |
| dielectric strength | 短时·23℃·1/8时 | ASTM D-149 | 17 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/1401X06 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 120 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 85 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | 缺口，-40℃ | ASTM D-256 | 3.5 kg·cm/cm |
| 缺口，23℃ | ASTM D-256 | 4.4 kg·cm/cm | |
| Flexural modulus | ASTM D790/ISO 178 | 2.5 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D-785 | 75 M标度 | |
| compressive strength | 23℃ | ASTM D-695 | 900 kg/cm |
| coefficient of friction | 0.17 | ||
| Tensile modulus | 23°C | ISO 527-2 | 2700 Mpa |
| elongation at break | ASTM D638/ISO 527 | 100 % | |
| Rockwell hardness | ASTM D785 | M75 | |
| tensile strength | ASTM D638/ISO 527 | 55 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | 无缺口，23℃ | ASTM D-256 | 不破裂 kg·cm/cm |
| Friction coefficient - vs. Metal | SuzukiMethod | 0.13 | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 30 % |
| bending strength | 23°C | ISO 178 | 90.0 Mpa |
| 23℃ | ASTM D-790 | 900 kg/cm | |
| elongation at break | 23℃ | ASTM D-638 | 15 % |
| tensile strength | 屈服,23°C | ISO 527-2 | 55.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2500 Mpa |
| 23℃ | ASTM D-790 | 26 kg/cm | |
| tensile strength | 23℃ | ASTM D-638 | 600 kg/cm |
| Impact strength of cantilever beam gap | 无缺口，-40℃ | ASTM D-256 | 120 kg·cm/cm |
| other | Test Condition | Test Method | TORAY JAPAN/1401X06 |
|---|---|---|---|
| characteristic | 非增强标准级 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/1401X06 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.31 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.08 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/1401X06 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY JAPAN/1401X06 |
|---|---|---|---|
| Heat distortion temperature | 18.6kg/cm | ASTM D-648 | 58 °C |
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 2.3 % |
| coefficient of friction | 本身 | ASTM D-1894 | 0.17 |
| Shrinkage rate | MD:3.00mm4 | 内部方法 | 1.7 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.080 % |
| coefficient of friction | 金属 | ASTM D-1894 | 0.13 |
| Heat distortion temperature | 4.6kg/cm | ASTM D-648 | 154 °C |
| Taber abraser | 1.000g·CS-17 | ASTM D-1044 | 10 毫克/1.000m |
| Shrinkage rate | 80×80×3板材 | 1.7-2.3 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/1401X06 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 60 1.8Mpa ℃（℉） |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 150 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 60.0 °C | |
| Linear coefficient of thermal expansion | ASTM D-696 | 9.4 cm/cm℃×10 | |
| MD：-30到100°C | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
| ASTM D696/ISO 11359 | 9.4*10^-5 mm/mm.℃ |