PA6 73M30 NC010 DUPONT USA
Zytel®
Automotive sector、Electronic field、Electrical field
Thermal stability、Easy electroplating
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/73M30 NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 110 kJ/m² |
| -30°C | ISO 179/1eU | 85 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/73M30 NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 4800 Mpa | |
| Tensile creep modulus | 1hr | ISO 899-1 | -- Mpa |
| Flexural modulus | ISO 178 | 4800 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 15 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | -- Mpa |
| Tensile modulus | ASTM D638/ISO 527 | 4800 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | 断裂 | ISO 527-2 | 82.0 Mpa |
| other | Test Condition | Test Method | DUPONT USA/73M30 NC010 |
|---|---|---|---|
| characteristic | 低翘曲性 热稳定性 |
| Physical properties | Test Condition | Test Method | DUPONT USA/73M30 NC010 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.9 % | |
| density | ASTM D792/ISO 1183 | 1.35 |
| flammability | Test Condition | Test Method | DUPONT USA/73M30 NC010 |
|---|---|---|---|
| FMVSS flammability | FMVSS302 | SE | |
| Flammability level | 0.8mm | IEC 60695-11-10,-20 | HB |
| UL flame retardant rating | 0.9mm | UL 94 | HB |
| physical property | Test Condition | Test Method | DUPONT USA/73M30 NC010 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.90 % |
| MD | ISO 294-4 | 0.90 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 6.3 % |
| 平衡,23°C,2.00mm,50%RH | ISO 62 | 2.1 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/73M30 NC010 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| melting temperature | ISO 11357-3 | 221 °C | |
| Linear coefficient of thermal expansion | MD：55to160°C | ISO 11359-2 | 8.9E-05 cm/cm/°C |
| TD：-- | ISO 11359-2 | 6.5E-05 cm/cm/°C | |
| MD：-40to23°C | ISO 11359-2 | 5.6E-05 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 5.7E-05 cm/cm/°C | |
| MD：-- | ISO 11359-2 | 6.3E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 195 °C |
| Linear coefficient of thermal expansion | TD：55to160°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| vicat | ISO 306/B50 | 210 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 80.0 °C |