Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HPX4EU SABIC INNOVATIVE US
LEXAN™
Drug application、Medical devices、Medical and nursing suppl、medicine、Medical/nursing supplies
Middle flow、Biocompatibility、Steam sterilization
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HPX4EU |
|---|---|---|---|
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 119 °C | |
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 124 °C | |
| RTIElec | UL746 | 130 °C | |
| Flow:-40 to 95°C | ASTME831 | 7.9E-05 cm/cm/°C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| RTI | UL746 | 130 °C | |
| Flow:23 to 80°C | ISO11359-2 | 7.9E-05 cm/cm/°C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/HPX4EU |
|---|---|---|---|
| Rockwell Hardness | L计秤 | ASTMD785 | 90 |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/HPX4EU |
|---|---|---|---|
| Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.40到0.80 % |
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.093 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 10 g/10min |
| Modeling Shrinkage | TD:3.20mm | 内部方法 | 0.40到0.80 % |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 9.50 cm3/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.24 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HPX4EU |
|---|---|---|---|
| ASTMD638 | 2220 Mpa | ||
| Break | ASTMD638 | 64.1 Mpa | |
| fracture | ISO527-2/50 | 120 % | |
| Break | ASTMD638 | 130 % | |
| Yield,50.0mm Span | ASTMD790 | 94.3 Mpa | |
| yield | ISO527-2/50 | 5.5 % | |
| Yield | ASTMD638 | 5.8 % | |
| 50.0mm Span | ASTMD790 | 2220 Mpa | |
| fracture | ISO527-2/50 | 61.5 Mpa | |
| ISO178 | 90.2 Mpa | ||
| Yield | ASTMD638 | 58.0 Mpa | |
| yield | ISO527-2/50 | 57.9 Mpa |
| Optical | Test Condition | Test Method | SABIC INNOVATIVE US/HPX4EU |
|---|---|---|---|
| Transmittance | 2540µm | ASTMD1003 | 82.0 % |
| Haze | 2540µm | ASTMD1003 | 3.0 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HPX4EU |
|---|---|---|---|
| Instrumented Dart Impact | -30°C,TotalEnergy | ASTMD3763 | 85.0 J |
| 23°C,TotalEnergy | ASTMD3763 | 82.4 J |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/HPX4EU |
|---|---|---|---|
| Flame Rating | 2.50mm | UL94 | V-2 |
| Glow Wire Ignition Temperature | 3.00mm | IEC60695-2-13 | 825 °C |
| 0.800mm | IEC60695-2-13 | 825 °C | |
| Flame Rating | 1.50mm | UL94 | HB |
| Glow Wire Flammability Index | 3.00mm | IEC60695-2-12 | 960 °C |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/HPX4EU |
|---|---|---|---|
| Surface Resistivity | ASTMD257 | >1.0E+15 ohms | |
| Volume Resistivity | ASTMD257 | >1.0E+15 ohms·cm |