PEEK 550CA20 JILIN JOINATURE
ZYPEEK®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JILIN JOINATURE/550CA20 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 有缺口 | ISO 180-A | 8 kJ/m² |
| ISO 180/U | 40 kJ/m² | ||
| Charpy Notched Impact Strength | ISO 179/1eA | 7 kJ/m² | |
| ISO 179/1U | 45 kJ/m² |
| Mechanical properties | Test Condition | Test Method | JILIN JOINATURE/550CA20 |
|---|---|---|---|
| bending strength | 断裂，23℃ | ISO 178 | 310 Mpa |
| Flexural modulus | 23℃ | ISO 178 | 16000 Mpa |
| tensile strength | 断裂，23℃ | ISO 527 | 205 Mpa |
| Shore hardness | 23℃ | ISO 868 | 86 D 级 |
| Tensile strain | 断裂，23℃ | ISO 527 | 2 % |
| Electrical performance | Test Condition | Test Method | JILIN JOINATURE/550CA20 |
|---|---|---|---|
| Volume resistivity | 23 ℃，1V | IEC 60093 | 10^7 ohms·cm |
| physical property | Test Condition | Test Method | JILIN JOINATURE/550CA20 |
|---|---|---|---|
| density | 结晶 | ISO 1183 | 1.37 g/cm³ |
| Shrinkage rate | TD | ISO 294-4 | 0.2 % |
| MD | ISO 294-4 | 0.7 % | |
| Water absorption rate | 23℃，24hr，3.20 mm | ISO 62-1 | 0.05 % |
| melt mass-flow rate | 380℃，5.0kg | ISO 1133 | 7 g/10min |
| Water absorption rate | 平衡，23℃，3.20 mm | ISO 62-1 | 0.4 % |
| Thermal performance | Test Condition | Test Method | JILIN JOINATURE/550CA20 |
|---|---|---|---|
| Heat distortion temperature | 1.8 Mpa，HDT | ISO 75-f | 325 °C |
| Linear coefficient of thermal expansion | 低于Tg沿着流动方向 | ISO 11359 | 8 ppm/K |
| Glass Transition Temperature | 起始 | ISO 11357 | 143 °C |
| melting temperature | ISO 11357 | 343 °C | |
| thermal conductivity | 23℃ | ISO 22007-4 | 0.95 W/m/K |
| specific heat | 23℃ | DSC | 1.8 kJ/kg/℃ |
| Linear coefficient of thermal expansion | 高于Tg沿着流动方向 | ISO 11359 | 8 ppm/K |