MMW-HDPE TOTAL Polyethylene HDPE 6410 TOTAL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | TOTAL/TOTAL Polyethylene HDPE 6410 |
|---|---|---|---|
| Tensile strain | Break,25µm,BlownFilm | ASTM D882A | 700 % |
| Water Vapor Transmission Rate | 38°C,25µm,BlownFilm | ASTMF1249 | 6.2 g/m²/24hr |
| Elmendorf tear strength | 25µm,BlownFilm，MD | ASTM D1922 | 24 g |
| tensile strength | Break,25µm,BlownFilm | ASTM D882A | 23.4 MPa |
| Yield,25µm,BlownFilm | ASTM D882A | 27.6 MPa | |
| Secant modulus | 2%Secant,MD:25µm,BlownFilm | ASTM D882A | 689 MPa |
| film thickness | 25 µm | ||
| Tensile strain | Break,25µm,BlownFilm，MD | ASTM D882A | 700 % |
| Elmendorf tear strength | 25µm,BlownFilm，TD | ASTM D1922 | 390 g |
| Secant modulus | 2%Secant,TD:25µm,BlownFilm | ASTM D882A | 703 MPa |
| 1%正割,MD:25µm,吹塑薄膜 | ASTM D882A | 862 MPa | |
| 1%正割,TD:25µm,吹塑薄膜 | ASTM D882A | 883 MPa |
| optical performance | Test Condition | Test Method | TOTAL/TOTAL Polyethylene HDPE 6410 |
|---|---|---|---|
| Haze ratio | 25.4µm,吹塑薄膜 | ASTM D1003 | 15 % |
| Gardner glossiness | 25.4µm,BlownFilm | ASTM D523 | 50 |
| physical property | Test Condition | Test Method | TOTAL/TOTAL Polyethylene HDPE 6410 |
|---|---|---|---|
| melt mass-flow rate | 190°C/21.6kg | ASTM D1238 | 33 g/10min |
| density | ASTM D792 | 0.961 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 1.2 g/10min |
| Thermal performance | Test Condition | Test Method | TOTAL/TOTAL Polyethylene HDPE 6410 |
|---|---|---|---|
| melting temperature | ASTM D3417 | 134 °C |