PA66 9950 BK SOLVAY USA
KALIX®
Fitness equipment、Automotive Applications
Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY USA/9950 BK |
|---|---|---|---|
| ISO 180 | 68 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/9950 BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 18500 Mpa | |
| Tensile stress | 屈服 | ISO 527-2 | 245 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.3 % |
| Flexural modulus | ISO 178 | 15900 Mpa | |
| Bending stress | 3.5% 应变 | ISO 178 | 379 Mpa |
| Electrical performance | Test Condition | Test Method | SOLVAY USA/9950 BK |
|---|---|---|---|
| Dissipation Factor | 2.40 GHz | ASTM D2520 | 0.011 |
| dielectric constant | 1.00 GHz | ASTM D2520 | 4.15 |
| 2.40 GHz | ASTM D2520 | 4.15 | |
| Dissipation Factor | 1.00 GHz | ASTM D2520 | 0.011 |
| flammability | Test Condition | Test Method | SOLVAY USA/9950 BK |
|---|---|---|---|
| 0.60 mm, All Colors | HB |
| physical property | Test Condition | Test Method | SOLVAY USA/9950 BK |
|---|---|---|---|
| Water absorption rate | 24 hr, 23°C | ASTM D570 | 0.37 % |
| Shrinkage rate | 横向流量 | 内部方法 | 0.32 % |
| 流量 | 内部方法 | 0.13 % |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/9950 BK |
|---|---|---|---|
| 0.45 MPa, 未退火 | ISO 75-2/B | 262 °C | |
| melting temperature | ASTM D3418 | 260 °C | |
| 1.8 MPa, 未退火 | ISO 75-2/A | 254 °C |
| injection | Test Condition | Test Method | SOLVAY USA/9950 BK |
|---|---|---|---|
| Temperature | 80 到 120 °C | ||
| Temperature at the rear of the barrel | 250 °C | ||
| Processing (melt) temperature | 285 到 305 °C | ||
| drying temperature | 80 °C | ||
| Temperature at the front of the material cylinder | 280 °C | ||
| drying time | 4.0 到 12 hr | ||
| Suggested maximum moisture content | 0.090 % |