ASA/PC XP4034 WH8B108 SABIC INNOVATIVE US

GELOY™

Automotive sector

Thermal stability,High mobility,Antistatic,Weather resistance

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE US/XP4034 WH8B108
Rockwell hardness	R-Scale	ASTM D785	110

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE US/XP4034 WH8B108
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	115 °C
		0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span7	ISO 75-2/Bf	116 °C
		1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span7	ISO 75-2/Af	98.0 °C
		1.8 MPa, Unannealed, 6.40 mm	ASTM D648	104 °C
Linear coefficient of thermal expansion	Across Flow : -20 to 150°C	ASTM E831	7.2E-5 cm/cm/°C
Linear coefficient of thermal expansion		Flow : -20 to 150°C	ASTM E831	7.2E-5 cm/cm/°C
thermal conductivity		ASTM C177	0.25 W/m/K
Vicat softening temperature		ISO 306/B50	113 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE US/XP4034 WH8B108
Bending modulus	50.0 mm Span3	ASTM D790	2510 Mpa
Bending modulus		--4	ISO 178	2500 Mpa
bending strength	Yield, 50.0 mm Span3	ASTM D790	88.0 Mpa
bending strength		--4,5	ISO 178	75.0 Mpa
Tensile modulus		ISO 527-2/1	2500 Mpa
Tensile strain	Break	ISO 527-2/50	130 %
		Break2	ASTM D638	25 %
		Yield	ISO 527-2/50	4.5 %
tensile strength	Yield	ISO 527-2/50	57.0 Mpa
		Break	ISO 527-2/50	50.0 Mpa
		Yield2	ASTM D638	62.0 Mpa

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE US/XP4034 WH8B108
melt mass-flow rate	260°C/5.0 kg	ASTM D1238	14 g/10 min
		220°C/10.0 kg	ASTM D1238	5.0 g/10 min
		280°C/3.8 kg	ASTM D1238	24 g/10 min
Outdoor applicability		UL 746C	f2
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.50 - 0.70 %
Shrinkage rate		Flow : 3.20 mm	Internal Method	0.50 - 0.70 %
Water absorption rate	24 hr	ASTM D570	0.25 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE US/XP4034 WH8B108
Dart impact	-30°C, Total Energy	ASTM D3763	30.0 J
Dart impact		23°C, Total Energy	ASTM D3763	47.0 J

flammability	Test Condition	Test Method	SABIC INNOVATIVE US/XP4034 WH8B108
UL flame retardant rating	1.5 mm	UL 94	HB

optical performance	Test Condition	Test Method	SABIC INNOVATIVE US/XP4034 WH8B108
gloss	60°, 无织构	ASTM D523	94

injection	Test Condition	Test Method	SABIC INNOVATIVE US/XP4034 WH8B108
Back pressure			0.300 to 1.00 Mpa
drying temperature			95 to 105 °C
drying time			3.0 to 4.0 hr
Exhaust hole depth			0.038 to 0.076 mm
Mold temperature			55 to 70 °C
Processing (melt) temperature			260 to 275 °C
Screw speed			30 to 80 rpm
Spray nozzle temperature			245 to 265 °C
Suggested injection volume			40 to 80 %
Suggested maximum moisture content			0.040 %
Temperature at the front of the material cylinder			250 to 265 °C
Temperature at the rear of the barrel			240 to 255 °C
Temperature in the middle of the barrel			245 to 260 °C