ABS Generic ABS+Nylon - Glass Fiber Generic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Generic/Generic ABS+Nylon - Glass Fiber |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 7.9to12 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 80to160 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 29to50 kJ/m² |
| hardness | Test Condition | Test Method | Generic/Generic ABS+Nylon - Glass Fiber |
|---|---|---|---|
| Rockwell hardness | 23°C | ASTM D785 | 116to118 |
| Mechanical properties | Test Condition | Test Method | Generic/Generic ABS+Nylon - Glass Fiber |
|---|---|---|---|
| tensile strength | 断裂,23°C | ASTM D638 | 51.0to124 MPa |
| Flexural modulus | 23°C | ISO 178 | 2550to6500 MPa |
| bending strength | 23°C | ASTM D790 | 75.8to207 MPa |
| Tensile modulus | 23°C | ISO 527-2 | 2500to5400 MPa |
| tensile strength | 屈服,23°C | ISO 527-2 | 43.0to56.4 MPa |
| Flexural modulus | 23°C | ASTM D790 | 2140to8320 MPa |
| elongation | 断裂,23°C | ASTM D638 | 3.8to4.0 % |
| bending strength | 23°C | ISO 178 | 60.0to167 MPa |
| physical property | Test Condition | Test Method | Generic/Generic ABS+Nylon - Glass Fiber |
|---|---|---|---|
| Shrinkage rate | 23°C | ISO 294-4 | 0.25to0.80 % |
| density | 23°C | ISO 1183 | 1.12to1.20 g/cm³ |
| Shrinkage rate | MD:23°C | ASTM D955 | 0.30to0.50 % |
| density | -- | ASTM D792 | 1.10to1.53 g/cm³ |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.70 % |
| Thermal performance | Test Condition | Test Method | Generic/Generic ABS+Nylon - Glass Fiber |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 107to202 °C |
| vicat | ISO 306 | 108to182 °C |