PA/MXD6 2502A MITSUBISHI ENGINEERING JAPAN
RENY™ 
Electronic and Electrical、Automotive sector
High rigidity、High impact、Filler: Glass mineral、20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/2502A
Impact strength of simply supported beam without notch23°CISO 17927 kJ/m²
Mechanical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/2502A
Tensile modulusISO 527-218400 Mpa
bending strengthISO 178249 Mpa
Tensile strain断裂ISO 527-21.2 %
Flexural modulusISO 17816500 Mpa
tensile strength 断裂ISO 527-2150 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/2502A
dielectric strength1.00mmIEC 60243-127 KV/mm
Volume resistivityIEC 600932E+16 ohms·cm
relative permittivity100HzIEC 60250--
Dissipation Factor100HzIEC 60250--
dielectric strength2.00mmIEC 60243-121 KV/mm
relative permittivity1MHzIEC 60250--
Surface ResistivityIEC 600935E+15 ohms
Dissipation Factor1MHzIEC 60250--
Compared to the Leakage Tracking Index (CTI)IEC 60112 V
flammabilityTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/2502A
UL flame retardant rating1.6mmUL 94V-0
physical property Test ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/2502A
Shrinkage rate0.49 %
Melt volume flow rate275°C/2.16kgISO 113314.0 cm3/10min
Water absorption rate平衡,23°C,50%RHISO 620.90 %
饱和,23°CISO 620.18 %
melt mass-flow rate275°C/2.16kgISO 113322 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/2502A
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B235 °C
1.8MPa,未退火，HDTISO 75-2/A217 °C
Linear coefficient of thermal expansionMDISO 11359-22E-05 cm/cm/°C
TDISO 11359-23E-05 cm/cm/°C