Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
MABS TR557 LG CHEM KOREA
--
--
--
RoHS
UL
MSDS
TDS
REACH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
MABS/LG CHEM KOREA/TR557
Melt mass flow rate
220°C/10.0 kg
ASTM D1238
g/10 min
2
Melt Mass Flow Rate (MFR) 220 ℃/10 kg
/
ASTM D 1238
g/10 min
2
Shrinkage rate - flow
23°C, 3.20 mm, 注塑
ASTM D955
%
0
Mechanical performance
Test Condition
Test Method
Unit
MABS/LG CHEM KOREA/TR557
Tensile modulus
23°C, 3.20 mm, 注塑
ASTM D638
Mpa
2
tensile strength
屈服, 23°C, 3.20 mm, 注塑
ASTM D638
Mpa
4
Tensile strength yield (yld)
3.2mm, 5
ASTM D638
kg/cm2
4
Tensile elongation fracture (brk)
3.2mm, 5
ASTM D638
%
3
Elongation rate
屈服, 23°C, 3.20 mm, 注塑
ASTM D638
%
>
Elongation rate
断裂, 23°C, 3.20 mm, 注塑
ASTM D638
%
1
Bending modulus
23°C, 3.20 mm, 注塑
ASTM D790
Mpa
2
Bending modulus
3.2mm, 1
ASTM D790
kg/cm2
2
bending strength
3.2mm, 1
ASTM D790
kg/cm2
7
bending strength
23°C, 3.20 mm, 注塑
ASTM D790
Mpa
7
Izod Notched at 23 ℃ (73 ℉)
3.2mm
ASTM D256
kg·cm/cm
1
Izod Notched at 23 ℃ (73 ℉)
6.4mm
ASTM D256
kg·cm/cm
1
Thermal performance
Test Condition
Test Method
Unit
MABS/LG CHEM KOREA/TR557
RTI
UL 746
°C
5
RTI Elec
UL 746
°C
5
RTI Imp
UL 746
°C
5
Hot deformation temperature
1.8 MPa, 未退火, 6.40 mm, 注塑
ASTM D648
°C
8
vicat softening point
ASTM D15257
°C
8
optical performance
Test Condition
Test Method
Unit
MABS/LG CHEM KOREA/TR557
Light transmittance
Rate B/50
ASTM D1003
%
9
Light transmittance
3200 µm, 注塑
ASTM D1003
%
9
Haze
注塑
ASTM D1003
%
2
Haze
-40°C to
ASTM D1003
%
2