Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS AC2300 FCFC TAIWAN
TAIRILOY®
Electrical field、Electronic field、Household appliances、Household appliances、Automotive sector
High impact resistance、heat-resisting、Easy electroplating、Plating grade、High heat resistance、General molding
UL
TDS
Processing
MSDS
UL
RoHS
SVHC
PSC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | FCFC TAIWAN/AC2300 |
|---|---|---|---|
| bending strength | 23 ℃ | ISO 178 | 86 Mpa |
| Impact strength of cantilever beam gap | 23 ℃ 3.2mm | ISO 180 | 540 J/m |
| Rockwell hardness | 23℃ | ISO 2039 - 2 | 110 R - scale |
| Charpy Notched Impact Strength | 23 ℃ 4mm | ISO 179 | 40 kJ/m² |
| Flexural modulus | 23 ℃ | ISO 178 | 2350 Mpa |
| tensile strength | 23 ℃ | ASTM D - 638 | 510 kg/cm2 |
| Flame retardant performance | Test Condition | Test Method | FCFC TAIWAN/AC2300 |
|---|---|---|---|
| UL flame retardant rating | 1.5 ~ 1.65 mm | UL - 94 | HB UL - 94 |
| physical property | Test Condition | Test Method | FCFC TAIWAN/AC2300 |
|---|---|---|---|
| melt mass-flow rate | 240℃ × 5kg | ISO 1133 | 9 g/10 min |
| density | 23℃/23℃ | ISO 1183 | 1.08 - |
| Shrinkage rate | 3.2mm | ISO 2577 | 0.4 ~ 0.6 % |
| melt mass-flow rate | 260℃ × 5kg | ISO 1133 | 21 g/10 min |
| Thermal performance | Test Condition | Test Method | FCFC TAIWAN/AC2300 |
|---|---|---|---|
| Heat distortion temperature | 1.8Mpa | ASTM D - 648 | 96 ℃ |
| vicat softening point | 10N ℃ | ISO 306 | 117 ℃ |