Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ASA C2950-7T1D300 SABIC INNOVATIVE NANSHA
CYCOLOY™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C2950-7T1D300 |
|---|---|---|---|
| Instrumented dart impact energy -30 ℃ (-22 ℉) peak | ASTM D3763 | 54 J | |
| ASTM D3763 | 61 J | ||
| Izod Notched at 23 ℃ (73 ℉) | ASTM D256 | 534 J/m | |
| Izod Notched -30 ℃ (-22 ℉) | ASTM D256 | 160 J/m |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C2950-7T1D300 |
|---|---|---|---|
| Rockwell hardness R | ASTM D785 | 123 R |
| Electrical Property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C2950-7T1D300 |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | UL 746A | 2 plc | |
| High current arc ignition (HAI) | UL 746A | 0 plc | |
| Dielectric Strength | in oil, 3.2 | ASTM D149 | 19.5 kV/mm |
| Volume resistivity | ASTM D257 | 100000000000000000 ohm-cm | |
| dielectric constant | ASTM D 150 | 3 | |
| Surface Resistivity | ASTM D257 | 10000000000000000 Ohm | |
| Dissipation Factor | ASTM D 150 | 49 E-4 | |
| Compared to the Leakage Traceability Index (CTI) | UL 746A | 0 plc | |
| arc resistance | ASTM D495 | 6 plc | |
| UL 746A | 1 plc |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C2950-7T1D300 |
|---|---|---|---|
| 2.6 mm/ | ASTM D790 | 102 Mpa | |
| Type I, 50 | ASTM D638 | 40 | |
| Tensile strength yield (yld) | Type I, 50 | ASTM D638 | 62 Mpa |
| Flexural modulus | 2.6 mm/ | ASTM D790 | 2650 Mpa |
| combustibility | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C2950-7T1D300 |
|---|---|---|---|
| UL fire rating 5VB | UL94 | 2.49 mm | |
| ASTM D 2863 | 32 % | ||
| UL fire rating V-0 | UL94 | 1.5 mm |
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C2950-7T1D300 |
|---|---|---|---|
| Vicat softening temperature | Rate B/50 | ASTM D1525 | 85 °C |
| Relative Temperature Index (RTI) intensity w/o impact- | UL 746B | 85 °C | |
| Coefficient of Linear Expansion (CLTE) Across Flow | -30°C to 3 | ASTM E831 | 72 E-6/°C |
| Relative Temperature Index (RTI) impact w/impact- | UL 746B | 85 °C | |
| Coefficient of Linear Expansion (CLTE) Longitudinal (Flow) | -30°C to 3 | ASTM E831 | 72 E-6/°C |
| thermal conductivity | ASTM C 177 | 0.2 W/m-°C | |
| Relative Temperature Index (RTI) Electrical Elec- | UL 746B | 85 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C2950-7T1D300 |
|---|---|---|---|
| Water absorption rate | 24 hours | ASTM D570 | 0.1 |
| Melt Mass Flow Rate (MFR) 260 ° C/2.16 kg | ASTM D1238 | 10 g/10min | |
| Longitudinal shrinkage rate (Flow) | xflow, 3.2 | Internal | 0.4~0.6 |
| Water absorption rate | flow, 3.2 | ASTM D570 | 0.4 |
| Longitudinal shrinkage rate (Flow) | flow, 3.2 | Internal | 0.4~0.8 |