Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO PKN4752-111S SABIC INNOVATIVE US
NORYL™
electromagnetic shielding
Conductive、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/PKN4752-111S |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 6.55 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/PKN4752-111S |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 3010 Mpa | |
| bending strength | 屈服,50.0mm跨距5 | ASTM D790 | 145 Mpa |
| elongation | 断裂 | ASTM D638 | 15 % |
| 屈服 | ASTM D638 | 6.0 % | |
| Flexural modulus | 100mmSpan4 | ASTM D790 | 2950 Mpa |
| 50.0mm跨距5 | ASTM D790 | 3150 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 73.8 Mpa |
| bending strength | Yield,100mmSpan4 | ASTM D790 | 137 Mpa |
| tensile strength | 屈服 | ASTM D638 | 86.2 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/PKN4752-111S |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.60-0.90 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/PKN4752-111S |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 152 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 5.6E-05 cm/cm/°C |
| vicat | ASTM D15256 | 174 °C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 161 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 6.3E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 151 °C |