PA6 K-FHGM35 DSM HOLAND
Akulon®
--
Mineral reinforcement、Thermal stability、High mobility、Glass fiber reinforced、enhance、Filler: DSM DSM Netherlan
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DSM HOLAND/K-FHGM35 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 35 kJ/m² |
| -30°C | ISO 179/1eU | 30 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DSM HOLAND/K-FHGM35 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 9000 Mpa | |
| bending strength | ISO 178 | 165 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.5 % |
| Flexural modulus | ISO 178 | 7700 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 120 Mpa |
| Electrical performance | Test Condition | Test Method | DSM HOLAND/K-FHGM35 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 5E-03 |
| relative permittivity | 100Hz | IEC 60250 | 3.50 |
| 1MHz | IEC 60250 | 3.30 | |
| Surface Resistivity | IEC 60093 | -- ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.014 |
| physical property | Test Condition | Test Method | DSM HOLAND/K-FHGM35 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.90 % |
| MD | ISO 294-4 | 0.30 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.7 % |
| 饱和,23°C | ISO 62 | 5.5 % |
| Thermal performance | Test Condition | Test Method | DSM HOLAND/K-FHGM35 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 220 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 215 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 205 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 3.5E-05 cm/cm/°C |
| TD | ISO 11359-2 | 5E-05 cm/cm/°C |