VLDPE SCLAIR® FP112-A NOVA Chemicals
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | NOVA Chemicals/SCLAIR® FP112-A |
|---|---|---|---|
| Low friction puncture | 51.0µm，吹膜 | 620 J/cm |
| film | Test Condition | Test Method | NOVA Chemicals/SCLAIR® FP112-A |
|---|---|---|---|
| Secant modulus | 51µm,BlownFilm | ASTM D882 | 123 MPa |
| elongation | 断裂,51µm,吹塑薄膜 | ASTM D882 | 640 % |
| Tensile strain | Break,51µm,BlownFilm | ASTM D882 | 890 % |
| Elmendorf tear strength | 51µm,BlownFilm，MD | ASTM D1922 | 710 g |
| Secant modulus | 51µm,吹塑薄膜 | ASTM D882 | 114 MPa |
| film thickness | 51 µm | ||
| tensile strength | Break,51µm,BlownFilm | ASTM D882 | 54.0 MPa |
| Dart impact | 51µm,BlownFilm | ASTM D1709A | >1000 g |
| tensile strength | Yield,51µm,BlownFilm | ASTM D882 | 7.00 MPa |
| Elmendorf tear strength | 51µm,BlownFilm，TD | ASTM D1922 | 1000 g |
| optical performance | Test Condition | Test Method | NOVA Chemicals/SCLAIR® FP112-A |
|---|---|---|---|
| gloss | 45°,51.0µm,BlownFilm | ASTM D2457 | 63 |
| Haze ratio | 51.0µm,BlownFilm | ASTM D1003 | 8.7 % |
| physical property | Test Condition | Test Method | NOVA Chemicals/SCLAIR® FP112-A |
|---|---|---|---|
| density | ASTM D792 | 0.912 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.90 g/10min |