ABS POLYLAC® PA-757GJ08 CHI MEI CORPORATION
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CHI MEI CORPORATION/POLYLAC® PA-757GJ08 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 20 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 19 kJ/m² |
| Mechanical properties | Test Condition | Test Method | CHI MEI CORPORATION/POLYLAC® PA-757GJ08 |
|---|---|---|---|
| Flexural modulus | ISO 178 | 2100 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 35 % |
| tensile strength | 屈服 | ISO 527-2/50 | 42.0 MPa |
| bending strength | ISO 178 | 63.0 MPa | |
| tensile strength | 断裂 | ISO 527-2/50 | 32.0 MPa |
| flammability | Test Condition | Test Method | CHI MEI CORPORATION/POLYLAC® PA-757GJ08 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | CHI MEI CORPORATION/POLYLAC® PA-757GJ08 |
|---|---|---|---|
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 29.0 cm³/10min |
| density | 23°C | ISO 1183 | 1.04 g/cm³ |
| Shrinkage rate | ISO 294-4 | 0.40to0.70 % |
| Thermal performance | Test Condition | Test Method | CHI MEI CORPORATION/POLYLAC® PA-757GJ08 |
|---|---|---|---|
| vicat | -- | ISO 306/A50 | 105 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 97.0 °C |
| vicat | -- | ISO 306/B50 | 99.0 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7.9E-05 cm/cm/°C |