Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 1101G-30 TORAY JAPAN
Toraycon®
Automotive sector,Electronic field,Electrical field
Glass fiber reinforced,Flame retardant,High impact resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 45 kJ/m² |
| hardness | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| Rockwell hardness | M计秤,23°C | ISO 2039-2 | 90 |
| Supplementary Information | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 9.60 CM |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 35 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 195 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 8800 kg/cm²(MPa)[Lb/in²] | |
| coefficient of friction | 0.19 | ||
| Tensile modulus | 23°C | ISO 527-2 | 10200 Mpa |
| elongation at break | ASTM D638/ISO 527 | 5 % | |
| Rockwell hardness | ASTM D785 | M91 | |
| tensile strength | ASTM D638/ISO 527 | 145 kg/cm²(MPa)[Lb/in²] | |
| Friction coefficient - vs. Metal | SuzukiMethod | 0.150 | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.5 % |
| bending strength | 23°C | ISO 178 | 220 Mpa |
| Flexural modulus | 23°C | ISO 178 | 9600 Mpa |
| tensile strength | 23°C | ISO 527-2 | 145 Mpa |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| dielectric constant | 23°C,50Hz | IEC 60250 | 3.70 |
| 23°C,1kHz | IEC 60250 | 4.20 | |
| dielectric strength | IEC 60243-1 | 36 KV/mm | |
| Volume resistivity | IEC 60093 | 5E+16 ohms·cm | |
| arc resistance | IEC 60950 | 120 sec | |
| Dissipation Factor | 23°C,50Hz | IEC 60250 | 2E-03 |
| Volume resistivity | ASTM D257/IEC 60093 | 2.5x10^14 Ω.cm | |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 0.020 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| other | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| characteristic | 30%玻璃纤维增强级.标准型号 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.55 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.07 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| UL flame retardant rating | 0.794mm | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| Shrinkage rate | TD:3.00mm1 | 内部方法 | 1.0 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.070 % |
| Shrinkage rate | MD:3.00mm2 | 内部方法 | 0.30 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/1101G-30 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 217 ℃（℉） |
| 1.8MPa, Not annealed | ISO 75-2/A | 213 °C | |
| Linear coefficient of thermal expansion | MD：-30到100°C | ISO 11359-2 | 4.1E-05 cm/cm/°C |
| 0.45MPa, Not annealed | ISO 75-2/B | 220 °C | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 2.0x10^-5 mm/mm.℃ |