Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PET DA003-8906K EASTMAN USA
Eastalloy™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EASTMAN USA/DA003-8906K |
|---|---|---|---|
| Multi axis Instrumented Impact Energy | -40°C,能量到力量峰值 | ISO 6603-2 | 23.0 J |
| 23°C,能量到力量峰值 | ISO 6603-2 | 19.0 J | |
| Dart impact | -40°C,EnergyatPeakLoad | ASTM D3763 | 46.0 J |
| 23°C,EnergyatPeakLoad | ASTM D3763 | 51.0 J |
| hardness | Test Condition | Test Method | EASTMAN USA/DA003-8906K |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 117 |
| Electrical performance | Test Condition | Test Method | EASTMAN USA/DA003-8906K |
|---|---|---|---|
| Dissipation Factor | 1kHz | ASTM D150 | 2E-03 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 mm/min |
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | ASTM D3638 | PLC 0 | |
| Surface Resistivity | ASTM D257 | 1E+16 ohms | |
| dielectric constant | 1kHz | ASTM D150 | 2.30 |
| Dissipation Factor | 1MHz | ASTM D150 | 8E-03 |
| dielectric strength | ASTM D149 | 17 KV/mm | |
| dielectric constant | 1MHz | ASTM D150 | 2.10 |
| arc resistance | ASTM D495 | 143 sec |
| Mechanical properties | Test Condition | Test Method | EASTMAN USA/DA003-8906K |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 150 % |
| 屈服 | ASTM D638 | 6.0 % | |
| bending strength | 屈服 | ASTM D790 | 86.0 Mpa |
| tensile strength | 屈服,4.00mm | ISO 527-2 | 56.0 Mpa |
| Flexural modulus | 4.00mm | ISO 178 | 2100 Mpa |
| Tensile strain | 断裂,4.00mm | ISO 527-2 | 130 % |
| tensile strength | 断裂 | ASTM D638 | 60.0 Mpa |
| 断裂,4.00mm | ISO 527-2 | 56.0 Mpa | |
| 屈服 | ASTM D638 | 56.0 Mpa | |
| Flexural modulus | ASTM D790 | 2140 Mpa | |
| bending strength | 4.00mm | ISO 178 | 81.0 Mpa |
| Tensile strain | Yield,4.00mm | ISO 527-2 | 5.4 % |
| optical performance | Test Condition | Test Method | EASTMAN USA/DA003-8906K |
|---|---|---|---|
| transmissivity | 总计 | ASTM D1003 | 81.0 % |
| Haze ratio | ASTM D1003 | 3.6 % | |
| transmissivity | Regular | ASTM D1003 | 77.0 % |
| flammability | Test Condition | Test Method | EASTMAN USA/DA003-8906K |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | V-2 |
| 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | EASTMAN USA/DA003-8906K |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.50-0.70 % |
| Water absorption rate | 24hr | ASTM D570 | 0.13 % |
| 23°C,24hr | ISO 62 | 0.13 % |
| Thermal performance | Test Condition | Test Method | EASTMAN USA/DA003-8906K |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 90.0 °C |
| specific heat | 60°C | DSC | 1380 J/kg/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 103 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 103 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 90.0 °C | |
| vicat | ASTM D15252 | 118 °C | |
| specific heat | 240°C | DSC | 2180 J/kg/°C |
| vicat | -- | ISO 306/B | 110 °C |
| -- | ISO 306/A | 118 °C |