Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM YF-5 BK JAPAN POLYPLASTIC
DURACON®
Fitness equipment,Automotive Applications
wear resistant,High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/YF-5 BK |
|---|---|---|---|
| ColorNumber | CF2001 |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/YF-5 BK |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1E+16 ohms |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/YF-5 BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2350 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 17 % | |
| bending strength | ISO 178 | 75.0 Mpa | |
| Flexural modulus | ISO 178 | 2200 Mpa | |
| tensile strength | ISO 527-2 | 55.0 Mpa |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/YF-5 BK |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/YF-5 BK |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 8.00 cm3/10min |
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 2.0 % |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 9.0 g/10min |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 2.0 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/YF-5 BK |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 1.2E-04 cm/cm/°C |
| MD：23到55°C | 内部方法 | 1.2E-04 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 87.0 °C |