PC+PPC LEXAN™ HPH4304 resin SABIC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC/LEXAN™ HPH4304 resin |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 50 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 130 J/m |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 120 J |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 600 J/m |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 12 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 11 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 45 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| Mechanical properties | Test Condition | Test Method | SABIC/LEXAN™ HPH4304 resin |
|---|---|---|---|
| elongation | 屈服 | ASTM D638 | 7.0 % |
| tensile strength | 屈服 | ASTM D638 | 64.0 MPa |
| Flexural modulus | ISO 178 | 2300 MPa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| bending strength | ISO 178 | 100 MPa | |
| tensile strength | 屈服 | ISO 527-2/50 | 65.0 MPa |
| elongation | 断裂 | ASTM D638 | >50 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 95.0 MPa |
| tensile strength | 断裂 | ASTM D638 | 69.0 MPa |
| Tensile modulus | ASTM D638 | 2100 MPa | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2200 MPa |
| Tensile strain | 断裂 | ISO 527-2/50 | 85 % |
| Tensile modulus | ISO 527-2/1 | 2150 MPa | |
| tensile strength | 断裂 | ISO 527-2/50 | 60.0 MPa |
| physical property | Test Condition | Test Method | SABIC/LEXAN™ HPH4304 resin |
|---|---|---|---|
| Melt volume flow rate | 330°C/2.16kg | ISO 1133 | 40.0 cm³/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.60to0.80 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.35 % |
| 饱和,23°C | ISO 62 | 0.16 % | |
| density | ASTM D792 | 1.20 g/cm³ | |
| ISO 1183 | 1.20 g/cm³ | ||
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 8.0 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC/LEXAN™ HPH4304 resin |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 153 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| TD：-40到40°C | ASTME831 | 8E-05 cm/cm/°C | |
| vicat | -- | ISO 306/B50 | 151 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 8E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 8E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 134 °C |
| vicat | ASTM D152510 | 162 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 139 °C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |