Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

POM UV90Z XAP2 CELANESE USA
CELCON®
Bottle cap,Electrical applications
Chemical resistance,antioxidant,Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | CELANESE USA/UV90Z XAP2 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 6.0 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 100 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.7 kJ/m² |
Mechanical properties | Test Condition | Test Method | CELANESE USA/UV90Z XAP2 |
---|---|---|---|
Tensile strain | 屈服 | ISO 527-2/1A/50 | 9.0 % |
Tensile modulus | ISO 527-2/1A/1 | 2700 Mpa | |
Flexural modulus | 23°C | ISO 178 | 2470 Mpa |
tensile strength | 屈服,23°C | ASTM D638 | 60.7 Mpa |
屈服 | ISO 527-2/1A/50 | 64.0 Mpa |
physical property | Test Condition | Test Method | CELANESE USA/UV90Z XAP2 |
---|---|---|---|
Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 8.00 cm3/10min |
Shrinkage rate | TD | ISO 294-4 | 1.7 % |
MD | ASTM D955 | 2.2 % | |
MD | ISO 294-4 | 1.9 % | |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
饱和,23°C | ISO 62 | 0.75 % | |
density | ASTM D792 | 1.41 g/cm³ | |
Shrinkage rate | TD | ASTM D955 | 1.8 % |
density | ISO 1183 | 1.41 g/cm³ |
Thermal performance | Test Condition | Test Method | CELANESE USA/UV90Z XAP2 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTM D648 | 110 °C |
melting temperature | ISO 11357-3 | 165 °C | |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 155 °C |
1.8MPa,未退火,HDT | ISO 75-2/A | 91.0 °C | |
melting temperature | ASTM D3418 | 165 °C | |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.1E-04 cm/cm/°C |
TD | ISO 11359-2 | 1.2E-04 cm/cm/°C |