PP 55T1030S-10000 SABIC INNOVATIVE SHANGHAI
SABIC®
medical care
Block copolymer
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/55T1030S-10000 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C,注塑 | ISO 179/1eU | 13 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/55T1030S-10000 |
|---|---|---|---|
| Shore hardness | 邵氏D,注塑 | ISO 868 | 68 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/55T1030S-10000 |
|---|---|---|---|
| Tensile strain | 断裂,3.20mm,注塑 | ISO 527-2/5/50 | 80 % |
| Flexural modulus | 注塑 | ASTM D790 | 2300 Mpa |
| tensile strength | 断裂,3.20mm,注塑 | ISO 527-2/5/50 | 18.0 Mpa |
| 屈服,3.20mm,注塑 | ISO 527-2/5/50 | 24.0 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/55T1030S-10000 |
|---|---|---|---|
| Shrinkage rate | 24小时 | 内部方法 | 1.0 % |
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 4.0 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/55T1030S-10000 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 6E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 120 °C |
| Linear coefficient of thermal expansion | MD：23到80°C | ASTM D696 | 7E-05 cm/cm/°C |
| vicat | ISO 306/A | 150 °C |