Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS BDT5510-1000 SABIC INNOVATIVE US
CYCOLAC™
Automotive sector、Automotive interior parts
Low gloss
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/BDT5510-1000 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 13 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 290 J/m |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7.2 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 kJ/m² |
| 23°C | ISO 180/1A | 13 kJ/m² | |
| Dart impact | 23°C | ASTM D3029 | 35.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/BDT5510-1000 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2930 Mpa | |
| ASTM D638 | 2280 Mpa | ||
| tensile strength | 屈服 | ISO 527-2/50 | 43.0 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 81.0 Mpa |
| ISO 178 | 67.0 Mpa | ||
| Flexural modulus | ISO 178 | 2030 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 53.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2460 Mpa |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/BDT5510-1000 |
|---|---|---|---|
| gloss | 60°,无织构 | ASTM D523 | 25 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/BDT5510-1000 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/BDT5510-1000 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.80 % |
| melt viscosity | 260°C,1000sec^-1 | ASTM D3835 | 163 Pa·s |
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 6.0 g/10min |
| spiral flow length | 内部方法 | 73.7 CM | |
| density | ASTM D792 | 1.05 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 14 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/BDT5510-1000 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 95.0 °C |
| vicat | ISO 306/B50 | 98.0 °C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 92.0 °C |
| 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 83.0 °C | |
| Linear coefficient of thermal expansion | MD：-40到60°C | ASTME831 | 1.4E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 81.0 °C |