PBT 3300 PBT vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PBT JAPAN POLYPLASTIC 3300

Enhanced level

US$ 3,130 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	JAPAN POLYPLASTIC/3300
bending strength		ISO 178	220 Mpa
Tensile strain	Break	ISO 527-2	2.2 %
Charpy Notched Impact Strength		ASTM D256/ISO 179	93 kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Notched侧	ASTM D-256	93 J/m
elongation		ASTM D-638	2.5 %
bending strength		ASTM D-790	210 Mpa
bending strength			ASTM D790/ISO 178	210 kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	2.5 %
Bending modulus		ISO 178	9030 Mpa
tensile strength		ISO 527-2	140 Mpa
tensile strength			ASTM D638/ISO 527	132 kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	9120 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap	反Notched侧	ASTM D-256	530 J/m
Bending modulus		ASTM D-790	9120 Mpa
tensile strength		ASTM D-638	132 Mpa
Electrical performance	Test Condition	Test Method	JAPAN POLYPLASTIC/3300
Dielectric strength	3.00mm	IEC 60243-1	23 KV/mm
Dielectric strength		2mmt	ASTM D-149	23 MV/m
Volume resistivity	3mmt	ASTM D-257	5×10 Ω.cm
Compared to the anti leakage trace index		IEC 60112	PLC 2
Volume resistivity		IEC 60093	5E+16 ohms·cm
Volume resistivity			ASTM D257/IEC 60093	5×1016 Ω.cm
thermal performance	Test Condition	Test Method	JAPAN POLYPLASTIC/3300
Hot deformation temperature	HDT	ASTM D648/ISO 75	213 ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	2-7 mm/mm.℃
		TD：23to55°C	Internal Method	9E-05 cm/cm/°C
		MD：23to55°C	Internal Method	2E-05 cm/cm/°C
UL flame retardant rating		UL 94	HB
Hot deformation temperature	1.82MPa	ASTM D-648	213 °C
Hot deformation temperature		1.8MPa,Unannealed	ISO 75-2/A	213 °C
Linear expansion coefficient (room temperature)			2-7
Physical properties	Test Condition	Test Method	JAPAN POLYPLASTIC/3300
Water absorption rate	23°C,24hr	ISO 62	0.10 %
density		ASTM D792/ISO 1183	1.53
Supplementary Information	Test Condition	Test Method	JAPAN POLYPLASTIC/3300
ColourNumber			EF2001/ED3002
flammability	Test Condition	Test Method	JAPAN POLYPLASTIC/3300
UL flame retardant rating		UL 94	HB
hardness	Test Condition	Test Method	JAPAN POLYPLASTIC/3300
Rockwell hardness	M-Scale	ISO 2039-2	100