Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 3300 JAPAN POLYPLASTIC
DURANEX®
Automotive sector
Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/3300 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 100 |
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/3300 |
|---|---|---|---|
| ColorNumber | EF2001/ED3002 |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/3300 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 210 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 9120 kg/cm²(MPa)[Lb/in²] | |
| ASTM D-790 | 9120 Mpa | ||
| bending strength | ASTM D-790 | 210 Mpa | |
| elongation | ASTM D-638 | 2.5 % | |
| elongation at break | ASTM D638/ISO 527 | 2.5 % | |
| tensile strength | ASTM D-638 | 132 Mpa | |
| ASTM D638/ISO 527 | 132 kg/cm²(MPa)[Lb/in²] | ||
| ISO 527-2 | 140 Mpa | ||
| bending strength | ISO 178 | 220 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.2 % |
| Flexural modulus | ISO 178 | 9030 Mpa | |
| Impact strength of cantilever beam gap | 缺口侧 | ASTM D-256 | 93 J/m |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 93 kg·cm/cm(J/M)ft·lb/in | |
| Impact strength of cantilever beam gap | 反缺口侧 | ASTM D-256 | 530 J/m |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/3300 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| Volume resistivity | IEC 60093 | 5E+16 ohms·cm | |
| dielectric strength | 2mmt | ASTM D-149 | 23 MV/m |
| Volume resistivity | 3mmt | ASTM D-257 | 5×10 Ω.cm |
| dielectric strength | 3.00mm | IEC 60243-1 | 23 KV/mm |
| Volume resistivity | ASTM D257/IEC 60093 | 5×1016 Ω.cm |
| Physical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/3300 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.53 |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/3300 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/3300 |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.10 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/3300 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 9E-05 cm/cm/°C |
| MD：23到55°C | 内部方法 | 2E-05 cm/cm/°C | |
| Heat distortion temperature | 1.82MPa，HDT | ASTM D-648 | 213 °C |
| HDT | ASTM D648/ISO 75 | 213 ℃（℉） | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 213 °C | |
| Linear expansion coefficient (room temperature) | 2-7 | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 2-7 mm/mm.℃ | |
| UL flame retardant rating | UL 94 | HB |