Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PET 530 NC010 DUPONT USA

Rynite®

Electrical field,Electronic field,Household appliances,Household appliances,Automotive sector

enhance,Glass fiber reinforced,wear resistant,High rigidity,High temperature resistan,Filler: Glass fiber reinf,30% filler by weight

Plastic Datasheets

thermal performance	Test Condition	Test Method	DUPONT USA/530 NC010
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	243 °C
Hot deformation temperature		1.8MPa,Unannealed	ISO 75-2/A	225 °C
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	1.9E-05 cm/cm/°C
		TD：-40to23°C	ISO 11359-2	6.8E-05 cm/cm/°C
		MD：-40to23°C	ISO 11359-2	2.2E-05 cm/cm/°C
		TD：--	ISO 11359-2	9.2E-05 cm/cm/°C
Melting temperature		ISO 11357-3	252 °C
RTI Elec	3.0mm	UL 746	155 °C
		0.40mm	UL 746	155 °C
		0.75mm	UL 746	155 °C
		1.5mm	UL 746	155 °C
RTI Imp	1.5mm	UL 746	155 °C
		3.0mm	UL 746	155 °C
		0.75mm	UL 746	155 °C
		0.40mm	UL 746	155 °C
RTI Str	0.40mm	UL 746	155 °C
		EffectiveThermalDiffusivity	UL 746	1.1E-07 m²/s
		3.0mm	UL 746	155 °C
		1.5mm	UL 746	155 °C
		0.75mm	UL 746	155 °C
Vicat softening temperature		ISO 306/B50	220 °C

mechanical properties	Test Condition	Test Method	DUPONT USA/530 NC010
Bending modulus		ISO 178	10500 Mpa
Tensile creep modulus	1hr	ISO 899-1	11200 Mpa
Tensile creep modulus		1000hr	ISO 899-1	9700 Mpa
Tensile modulus		ISO 527-2	11500 Mpa
Tensile strain	Break	ISO 527-2	2.0 %
tensile strength	Break	ISO 527-2	135 Mpa

Electrical performance	Test Condition	Test Method	DUPONT USA/530 NC010
Compared to the anti leakage trace index		IEC 60112	PLC 3
Compared to the anti leakage trace index		CTI	UL 746	PLC 2
Dielectric strength		IEC 60243-1	39 KV/mm
Dissipation factor	1MHz	IEC 60250	0.013
Dissipation factor		100Hz	IEC 60250	7E-03
Relative permittivity	100Hz	IEC 60250	4.80
Relative permittivity		1MHz	IEC 60250	4.30
Surface resistivity		IEC 60093	1E+14 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm

Physical properties	Test Condition	Test Method	DUPONT USA/530 NC010
density		ISO 1183	1.68 g/cm³
Melt Volume Flow Rate (MVR)	280°C/2.16kg	ISO 1133	6.00 cm3/10min
Shrinkage rate	MD	ISO 294-4	0.20 %
Shrinkage rate		TD	ISO 294-4	0.80 %
Top out temperature			170 °C
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.15 %
Water absorption rate		Saturation,23°C,2.00mm	ISO 62	0.75 %

impact performance	Test Condition	Test Method	DUPONT USA/530 NC010
Charpy Notched Impact Strength	23°C	ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength		-30°C	ISO 179/1eA	9.0 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	40 kJ/m²
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	40 kJ/m²

flammability	Test Condition	Test Method	DUPONT USA/530 NC010
Extreme Oxygen Index		ISO 4589-2	33 %
FMVSS flammability		FMVSS302	DNI
UL flame retardant rating	0.35mm	UL 94	V-0
		0.35mm	IEC 60695-11-10,-20	V-0
		1.5mm	IEC 60695-11-10,-20	V-0
		1.5mm	UL 94	V-0