PC/PBT
PC/PBT SABIC INNOVATIVE US X2500UV-GY1D562BZDD
Injection grade
US$ 2,740 / MT
FOB Guangzhou port, China
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/X2500UV-GY1D562BZDD
Vicat softening temperature--ASTMD152511135 °C
Ball Pressure Test125°CIEC 60695-10-2通过
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648108 °C
1.8MPa,Unannealed,64.0mmSpan11ISO 75-2/Af108 °C
0.45MPa,Unannealed,64.0mmSpan10ISO 75-2/Bf126 °C
1.8MPa,Unannealed,64.0mmSpan10ISO 75-2/Af108 °C
0.45MPa,Unannealed,64.0mmSpan11ISO 75-2/Bf126 °C
Vicat softening temperature--ISO 306/A50145 °C
--ASTMD152512135 °C
thermal conductivityISO 83020.18 W/m/K
Vicat softening temperature--ISO 306/B120136 °C
Linear coefficient of thermal expansionMD:-40to40°CASTME8318E-05 cm/cm/°C
MD:23to80°CISO 11359-28.2E-05 cm/cm/°C
TD:-40to40°CASTME8318.5E-05 cm/cm/°C
TD:23to80°CISO 11359-28.7E-05 cm/cm/°C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/X2500UV-GY1D562BZDD
elongationBreakASTM D638100 %
bending strengthYield,50.0mmSpan5ASTM D79079.0 Mpa
Yield,50.0mmSpan6ASTM D79079.0 Mpa
--ASTM D79079.0 Mpa
Taber abraser1000Cycles,1000g,CS-17WheelInternal Method20.0 mg
bending strength--7,8ISO 17880.0 Mpa
Bending modulus50.0mmSpan5ASTM D7902150 Mpa
50.0mmSpan6ASTM D7902150 Mpa
elongationBreakISO 527-2/5070 %
YieldASTMD6385.0 %
Yield5ASTM D6385.0 %
Yield4ASTM D6385.0 %
Break4ASTM D63880 %
Break5ASTM D63880 %
tensile strengthBreakISO 527-2/5056.0 Mpa
bending strength--6,7ISO 17880.0 Mpa
tensile strengthYield4ASTM D63856.0 Mpa
Yield5ASTM D63856.0 Mpa
YieldISO 527-2/5057.0 Mpa
Tensile modulus--3ASTM D6382200 Mpa
--4ASTM D6382200 Mpa
tensile strengthYieldASTM D63853.0 Mpa
Bending modulus--7ISO 1782150 Mpa
Tensile modulus--ISO 527-2/12200 Mpa
Bending modulus--6ISO 1782150 Mpa
tensile strengthBreak5ASTM D63855.0 Mpa
Break4ASTM D63855.0 Mpa
Bending modulus--ASTM D7902100 Mpa
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/X2500UV-GY1D562BZDD
melt mass-flow rate265°C/2.16kgASTM D12389.0 g/10min
Shrinkage rateMD3Internal Method0.50-0.80 %
MD2Internal Method0.50-0.80 %
MD:3.20mmInternal Method0.50-0.80 %
Melt Volume Flow Rate (MVR)265°C/1.2kgISO 11334.00 cm3/10min
Shrinkage rateTD2Internal Method0.50-0.80 %
TD3Internal Method0.50-0.80 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.20 %
Saturation,23°CISO 620.70 %
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/X2500UV-GY1D562BZDD
Dissipation factor50HzIEC 602502E-03
Relative permittivity50HzIEC 602503.30
Volume resistivityIEC 60093>1.0E+14 ohms·cm
Dissipation factor1MHzIEC 602500.020
60HzIEC 602502E-03
Surface resistivityIEC 60093>1.0E+15 ohms
Relative permittivity1MHzIEC 602503.10
60HzIEC 602503.30
Dielectric strength3.20mm,in OilIEC 60243-117 KV/mm
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/X2500UV-GY1D562BZDD
Burning wire flammability index2.7mmIEC 60695-2-12750 °C
UL flame retardant rating1.5mmUL 94HB
impact performanceTest ConditionTest MethodSABIC INNOVATIVE US/X2500UV-GY1D562BZDD
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Charpy Notched Impact Strength-30°CISO 179/1eA30 kJ/m²
23°CISO 179/1eA50 kJ/m²
Dart impact23°C,TotalEnergyASTM D376360.0 J
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
hardnessTest ConditionTest MethodSABIC INNOVATIVE US/X2500UV-GY1D562BZDD
Ball Pressure TestH358/30ISO 2039-195.0 Mpa

Supplier Join

Contact Us

Get App

Top

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index

+86 0755 27873515

Room 906, Global Digital Building, No. 9 Gaoxin Middle 3rd Road, Maling Community, Yuehai Subdistrict, Nanshan District, Shenzhen, Guangdong Province, China