Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DL-4040 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electronic and Electrical、Automotive components、Engine parts
Thermal stability、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DL-4040 |
|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 7.6E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 141 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 7.6E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 143 °C |
| Linear thermal expansion coefficient | MD：-40到40°C | ISO11359-2 | 7.7E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 128 °C |
| 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 129 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 7.7E-05 cm/cm/°C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DL-4040 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2060 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 29 % |
| Tensile Strain | ISO527-2/5 | 29 % | |
| Flexural Strength | ASTMD790 | 73.8 Mpa | |
| Coefficient of Friction | Dynamic | ASTMD3702Modified | 0.25 |
| Tensile Modulus | ISO527-2/1 | 2050 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 43.0 Mpa |
| Tensile Stress | 断裂 | ISO527-2/5 | 39.0 Mpa |
| Flexural Modulus | ISO178 | 1930 Mpa | |
| Coefficient of Friction | Static | ASTMD3702Modified | 0.21 |
| Tensile Elongation | 屈服 | ASTMD638 | 6.2 % |
| Specific Wear Rate | ASTMD3702Modified | 7.50 10^-10in^5-min/ft-lb-hr | |
| Flexural Stress | ISO178 | 63.0 Mpa | |
| Tensile Modulus | ASTMD638 | 2080 Mpa | |
| Tensile Strength | 断裂 | 39.0 Mpa | |
| Tensile Strain | 屈服 | ISO527-2/5 | 5.9 % |
| Tensile Stress | 44.0 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/DL-4040 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.36 % |
| 24hr,50%RH | ASTMD570 | 0.25 % | |
| Modeling Shrinkage | MD：24小时 | ASTMD955 | 0.50to0.70 % |
| TD：24hr | 0.60to0.80 % | ||
| TD:24小时 | ISO294-4 | 0.64 % | |
| MD:24小时 | 0.59 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DL-4040 |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | 180 kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 24.8 J |
| 23°C,EnergyatPeakLoad | 24.8 J | ||
| Notched Izod Impact Strength | 23°C | ISO180/1A | 12 kJ/m² |
| Multi-Axial Instrumented Impact Energy | ISO6603-2 | 21.1 J |