MS MM-60 DENKA JAPAN
--
Automotive interior parts、Automotive External Parts
transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | DENKA JAPAN/MM-60 |
|---|---|---|---|
| melt mass-flow rate | 220℃，10KG | ASTM D-1238 | 9 g/10min |
| density | ASTM D-792 | 1.13 |
| Mechanical properties | Test Condition | Test Method | DENKA JAPAN/MM-60 |
|---|---|---|---|
| Flexural modulus | 23℃ | ASTM D-790 | 3330（34000） MPa(KG/cm |
| bending strength | 23℃ | ASTM D-790 | 118（1200） MPa(KG/cm |
| Breaking stress | 23℃ | ASTM D-638 | 18 % |
| Impact strength of cantilever beam gap | 230℃，6.4mmt | ASTM D-256 | 27（2.8） J/m(kg.cm/cm) |
| Rockwell hardness | 23℃ | ASTM D-785 | 128 R scale |
| Tensile stress | 23℃，屈服 | ASTM D-638 | 69（700） MPa(KG/cm |
| processability | Test Condition | Test Method | DENKA JAPAN/MM-60 |
|---|---|---|---|
| Shrinkage rate | 200℃,5Kg | ASTM D-955 | 0.2-0.6 % |
| physical property | Test Condition | Test Method | DENKA JAPAN/MM-60 |
|---|---|---|---|
| transmissivity | 2.0mmt | ASTM D-1003 | 93 % |
| Haze ratio | 2.0mmt | ASTM D-1003 | 0.3 % |
| Thermal performance | Test Condition | Test Method | DENKA JAPAN/MM-60 |
|---|---|---|---|
| Heat distortion temperature | 1.82MPa，HDT | ASTM D-648 | 90 °C |
| combustibility | UL 94 | HB | |
| Linear coefficient of thermal expansion | 6.4mmt | ASTM D-696 | 7.0 |