PC 121R BK1E675 SABIC INNOVATIVE US
LEXAN™
Profile、building materials
Low viscosity、Flame retardant、transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/121R BK1E675 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 129 °C |
| Specific Heat | ASTMC351 | 1260 J/kg/°C | |
| RTIElec | UL746 | 130 °C | |
| Thermal Conductivity | ASTMC177 | 0.25 W/m/K | |
| RTIStr | UL746 | 130 °C | |
| Linear thermal expansion coefficient | MD：-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C |
| Evolution Calendar intelligent importer | UL746 | 130 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 138 °C |
| Vicat Softening Temperature | ASTMD15257 | 154 °C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/121R BK1E675 |
|---|---|---|---|
| Rockwell Hardness | R计秤 | ASTMD785 | 118 |
| M计秤 | ASTMD785 | 70 |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/121R BK1E675 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2340 Mpa |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 96.5 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 7.0 % |
| 断裂 | ASTMD638 | 130 % | |
| Tensile Strength | 屈服 | ASTMD638 | 62.1 Mpa |
| 断裂 | ASTMD638 | 68.9 Mpa | |
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17转轮 | ASTMD1044 | 10.0 mg |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/121R BK1E675 |
|---|---|---|---|
| Moisture Absorption | 24hr | ASTMD570 | 0.15 % |
| Outdoor Suitability | UL746C | f2 | |
| Density / Specific Gravity | ASTMD792 | 1.19 g/cm³ | |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 18 g/10min |
| Moisture Absorption | 平衡,23°C | ASTMD570 | 0.35 % |
| Specific Volume | ASTMD792 | 0.835 cm³/g | |
| Moisture Absorption | 平衡,100°C | ASTMD570 | 0.58 % |
| Optical | Test Condition | Test Method | SABIC INNOVATIVE US/121R BK1E675 |
|---|---|---|---|
| Transmittance | 2540µm | ASTMD1003 | 88.0 % |
| Index of Refraction | ASTMD542 | 1.586 | |
| Haze | 2540µm | ASTMD1003 | 1.0 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/121R BK1E675 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 11 kJ/m² |
| 23°C | ASTMD256 | 690 J/m | |
| 23°C | ASTMD4812 | 3200 J/m | |
| Tensile Impact Strength | ASTMD1822 | 546 kJ/m² | |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | NoBreak |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak |
| Gardner Impact | 23°C | ASTMD3029 | 169 J |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 12 kJ/m² |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | NoBreak |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 65 kJ/m² |
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 62.1 J |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 65 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/121R BK1E675 |
|---|---|---|---|
| Flame Rating | 0.70mm | UL94 | HB |
| Radiant Panel Listing | UL | YES |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/121R BK1E675 |
|---|---|---|---|
| Dielectric Constant | 60Hz | ASTMD150 | 3.17 |
| 50Hz | ASTMD150 | 3.17 | |
| Dissipation Factor? | 50Hz | ASTMD150 | 9E-04 |
| Volume Resistivity | ASTMD257 | >1.0E+17 ohms·cm | |
| Dissipation Factor? | 60Hz | ASTMD150 | 9E-04 |
| 1MHz | ASTMD150 | 0.010 | |
| Hot-wire Ignition | HWI | UL746 | PLC 2 |
| Dielectric Constant | 1MHz | ASTMD150 | 2.96 |
| Comparative Tracking Index | CTI | UL746 | PLC 2 |
| High Amp Arc Ignition | HAI | UL746 | PLC 1 |
| High Voltage Arc Tracking Rate | HVTR | UL746 | PLC 2 |
| Dielectric Strength | 3.20mm,inAir | ASTMD149 | 15 KV/mm |