PC+Polyester PRL PC/TP-FR2 Polymer Resources Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Polymer Resources Ltd./PRL PC/TP-FR2 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -40°C,3.18mm | ASTM D256 | 370 J/m |
| Dart impact | 3.18mm | ASTM D3029 | 36.2 J |
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 690 J/m |
| Mechanical properties | Test Condition | Test Method | Polymer Resources Ltd./PRL PC/TP-FR2 |
|---|---|---|---|
| Flexural modulus | 3.18mm | ASTM D790 | 2000 MPa |
| tensile strength | 屈服,3.18mm | ASTM D638 | 50.3 MPa |
| 断裂,3.18mm | ASTM D638 | 48.3 MPa | |
| bending strength | 3.18mm | ASTM D790 | 75.8 MPa |
| flammability | Test Condition | Test Method | Polymer Resources Ltd./PRL PC/TP-FR2 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | Polymer Resources Ltd./PRL PC/TP-FR2 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.60to0.90 % |
| melt mass-flow rate | 265°C/2.16kg | ASTM D1238 | 5.0to12 g/10min |
| density | ASTM D792 | 1.25 g/cm³ |
| Thermal performance | Test Condition | Test Method | Polymer Resources Ltd./PRL PC/TP-FR2 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.18mm，HDT | ASTM D648 | 90.6 °C |
| RTI Imp | 1.5mm | UL 746 | 75.0 °C |
| Heat distortion temperature | 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 82.2 °C |
| RTI Elec | 1.5mm | UL 746 | 75.0 °C |
| RTI | 1.5mm | UL 746 | 75.0 °C |