Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PK SCHULAKETON E A SCHULMAN USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON E |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
-30°C | ISO 179/1eA | 4.0 kJ/m² | |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
-30°C | ISO 179 | 80 kJ/m² |
Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON E |
---|---|---|---|
Tensile strain | 屈服 | ISO 527-2/1A/50 | 35 % |
bending strength | 3.5%应变 | ISO 178 | 55.0 MPa |
Tensile modulus | ISO 527-2/1A/1 | 2050 MPa | |
Flexural modulus | ISO 178 | 2350 MPa | |
tensile strength | 屈服 | ISO 527-2/1A/50 | 50.0 MPa |
Electrical performance | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON E |
---|---|---|---|
Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
flammability | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON E |
---|---|---|---|
Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
UL flame retardant rating | 0.8mm | UL 94,IEC60695-11-10,-20 | V-0 |
Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 960 °C |
Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 850 °C |
UL flame retardant rating | 0.40mm | UL 94,IEC60695-11-10,-20 | V-0 |
3.2mm | UL 94,IEC60695-11-10,-20 | V-0 | |
1.6mm | UL 94,IEC60695-11-10,-20 | V-0 | |
Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 825 °C |
Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 960 °C |
Limiting Oxygen Index | ISO 4589-2 | 33 % | |
Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 825 °C |
physical property | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON E |
---|---|---|---|
Melt volume flow rate | 240°C/2.16kg | ISO 1133 | 5.00 cm³/10min |
density | ISO 1183/A | 1.25 g/cm³ |
Thermal performance | Test Condition | Test Method | A SCHULMAN USA/SCHULAKETON E |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/Af | 112 °C |
vicat | -- | ISO 306/A50 | 214 °C |
-- | ISO 306/B50 | 184 °C | |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/Bf | 178 °C |