PA66 A3GK30 AKRO-PLASTIC GERMANY
AKROMID® 
Shell,Household appliances,Electronic field,Electrical field,Electrical appliances
Excellent appearance,Glass bead reinforcement,Low warpage,enhance,Filler: Glass beads,30%,Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodAKRO-PLASTIC GERMANY/A3GK30
Impact strength of simply supported beam without notch23°CISO 179/1eU28 kJ/m²
-30°CISO 179/1eU22 kJ/m²
Supplementary InformationTest ConditionTest MethodAKRO-PLASTIC GERMANY/A3GK30
ReinforcementContentISO 117230 %
Mechanical propertiesTest ConditionTest MethodAKRO-PLASTIC GERMANY/A3GK30
Tensile modulusISO 527-2/15000 Mpa
tensile strength 断裂ISO 527-2/590.0 Mpa
bending strengthISO 178140 Mpa
Flexural modulusISO 1784300 Mpa
Tensile strain断裂ISO 527-2/54.0 %
Fracture bending strainISO 1786.5 %
Electrical performanceTest ConditionTest MethodAKRO-PLASTIC GERMANY/A3GK30
Volume resistivityIEC 600931E+15 ohms·cm
Surface ResistivityIEC 600931E+13 ohms
Compared to the Leakage Tracking Index (CTI)解决方案AIEC 60112PLC 1
flammabilityTest ConditionTest MethodAKRO-PLASTIC GERMANY/A3GK30
burning rate1.00mmFMVSS302<100 mm/min
Burning wire flammability index1.6mmIEC 60695-2-12650 °C
UL flame retardant rating1.6mmUL 94HB
physical property Test ConditionTest MethodAKRO-PLASTIC GERMANY/A3GK30
Shrinkage rateTDISO 294-41.3 %
MDISO 294-41.2 %
moisture absorption70°C，62%RHISO 11102.0 %
Water absorption rate饱和,23°CISO 625.8 %
Thermal performanceTest ConditionTest MethodAKRO-PLASTIC GERMANY/A3GK30
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B225 °C
melting temperatureDIN EN11357-1262 °C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A100 °C