Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP E473i BK210P JAPAN POLYPLASTIC
LAPEROS®
Electrical applications、Home appliance components
enhance、Glass fiber reinforced
UL
MSDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/E473i BK210P |
|---|---|---|---|
| Rockwell hardness | M 计秤 | ISO 2039-2 | 55 |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/E473i BK210P |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 2.8 % |
| bending strength | ISO 178 | 160 Mpa | |
| Flexural modulus | ISO 178 | 11000 Mpa | |
| Bending Strain | ISO 178 | 2.8 % | |
| tensile strength | ASTM D638 | 125 Mpa |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/E473i BK210P |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 4 | |
| Dissipation Factor | 1 MHz | IEC 60250 | 0.030 |
| Volume resistivity | IEC 60093 | 1.0E+16 ohms·cm | |
| relative permittivity | 1 MHz | IEC 60250 | 3.70 |
| 1 kHz | IEC 60250 | 4.20 | |
| Dissipation Factor | 1 kHz | IEC 60250 | 0.020 |
| dielectric strength | 3.00 mm | IEC 60243-1 | 26 KV/mm |
| 1.00 mm | IEC 60243-1 | 53 KV/mm | |
| arc resistance | ASTM D495 | 151 sec |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/E473i BK210P |
|---|---|---|---|
| Color number | VF2201/BK210P | ||
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/E473i BK210P |
|---|---|---|---|
| Shrinkage rate | 横向流量 : 1.00 mm | 内部方法 | 0.39 % |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.020 % |
| Shrinkage rate | 流量 : 1.00 mm | 内部方法 | 0.030 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/E473i BK210P |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 275 °C |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 250 °C |