PC DCL-4523 SABIC INNOVATIVE US
LNP™ STAT-KON™
Automotive components、Electronic and electrical、Sports equipment
Thermal stability、High temperature resistan、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DCL-4523 |
|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 3.3E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 141 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 3.3E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 141 °C |
| Linear thermal expansion coefficient | MD：-40到40°C | ISO11359-2 | 3.7E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 138 °C |
| 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 137 °C | |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 3.7E-05 cm/cm/°C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/DCL-4523 |
|---|---|---|---|
| Moisture Absorption | 24hr,50%RH | ASTMD570 | 0.12 % |
| Modeling Shrinkage | MD：24小时 | ASTMD955 | 0.20 % |
| TD：24hr | ASTMD955 | 0.30 % | |
| TD:24小时 | ISO294-4 | 0.27 % | |
| MD:24小时 | ISO294-4 | 0.16 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DCL-4523 |
|---|---|---|---|
| Flexural Modulus | ISO178 | 10300 Mpa | |
| Tensile Elongation | 断裂 | ASTMD638 | 2.0 % |
| Flexural Modulus | ASTMD790 | 9100 Mpa | |
| Flexural Strength | ASTMD790 | 187 Mpa | |
| Tensile Modulus | ISO527-2/1 | 10200 Mpa | |
| Tensile Strain | 断裂 | ISO527-2 | 1.8 % |
| Tensile Stress | 断裂 | ISO527-2 | 123 Mpa |
| Flexural Stress | ISO178 | 186 Mpa | |
| Tensile Modulus | ASTMD638 | 10500 Mpa | |
| Tensile Strength | 断裂 | ASTMD638 | 121 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DCL-4523 |
|---|---|---|---|
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 16.1 J |
| 23°C | ISO180/1U | 27 kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO6603-2 | 3.19 J | |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 7.2 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/DCL-4523 |
|---|---|---|---|
| Flame Rating | 1.5mm,TestingbySABIC | UL94 | HB |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DCL-4523 |
|---|---|---|---|
| Surface Resistivity | ASTMD257 | 10to1.0E+6 ohms |