PC/ABS A35-110 STYRON US
PULSE™
Automotive sector、Automotive External Parts、Lighting applications、Automotive interior parts、Application in the automo
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | STYRON US/A35-110 |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eU2 | NoBreak |
| 23°C | ISO 179/1eU2 | NoBreak | |
| 23°C | ISO 179/1eA2 | 35.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | STYRON US/A35-110 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2350 Mpa | |
| tensile strength | 屈服 | ISO 527-2/5 | 58.0 Mpa |
| Tensile strain | 屈服 | ISO 527-22 | 4.8 % |
| Nominal fracture strain | ISO 527-22 | >50 % | |
| Flexural modulus | ISO 178 | 2200 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | >80 % |
| tensile strength | 屈服 | ISO 527-22 | 57.0 Mpa |
| Tensile modulus | ISO 527-22 | 2350 Mpa |
| flammability | Test Condition | Test Method | STYRON US/A35-110 |
|---|---|---|---|
| BurningBehav.at1.6mmnom.thickn | 1.60mm,UL | HB 4.21 | |
| Limiting Oxygen Index (LOI) | ISO 4589-22 | 21 % |
| physical property | Test Condition | Test Method | STYRON US/A35-110 |
|---|---|---|---|
| Apparent density | ISO 60 | 0.67 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 0.40-0.70 % | |
| melt mass-flow rate | 260°C/5.0kg | ISO 1133 | 14 g/10min |
| VOCContent | VDA277 | 9.00 µg/g | |
| spiral flow length | 45.0 CM |
| Thermal performance | Test Condition | Test Method | STYRON US/A35-110 |
|---|---|---|---|
| vicat | 50N | ISO 3062 | 132 °C |
| ISO 306/B50 | 132 °C | ||
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 110 °C |
| 1.8MPa，HDT | ISO 75-22 | 110 °C | |
| Linear coefficient of thermal expansion | MD：-30到80°C | ISO 11359-2 | 7.1E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa，HDT | ISO 75-22 | 130 °C |