Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM/PTFE FL2020 MITSUBISHI ENGINEERING JAPAN
Iupital™ 
Electronic and Electrical、Automotive sector
Weather resistance、Medium viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/FL2020
Impact strength of simply supported beam without notch23°CISO 17950 kJ/m²
Mechanical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/FL2020
Tensile modulusISO 527-22400 Mpa
Nominal tensile fracture strainISO 527-215 %
bending strengthISO 17867.0 Mpa
Flexural modulusISO 1782200 Mpa
Tensile strain屈服ISO 527-28.0 %
tensile strength 屈服ISO 527-244.0 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/FL2020
dielectric strength1.00mmIEC 60243-125 KV/mm
Volume resistivityIEC 600931E+14 ohms·cm
dielectric strength3.00mmIEC 60243-116 KV/mm
Surface ResistivityIEC 600931E+16 ohms
Compared to the Leakage Tracking Index (CTI)IEC 60112 V
flammabilityTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/FL2020
UL flame retardant rating0.800mmUL 94HB
0.8mmUL 94HB
physical property Test ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/FL2020
Melt volume flow rate190°C/2.16kgISO 11334.70 cm3/10min
Water absorption rate平衡,23°C,50%RHISO 620.18 %
melt mass-flow rate190°C/2.16kgISO 11336.0 g/10min
Shrinkage rateMD：3.00mm2.1 %
Thermal performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/FL2020
melting temperatureISO 11357-3166 °C
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B151 °C
1.8MPa,未退火，HDTISO 75-2/A96.0 °C
1.8MPa, Not annealedISO 75-2/A97.0 °C
Linear coefficient of thermal expansionMDISO 11359-21.1E-04 cm/cm/°C
0.45MPa, Not annealedISO 75-2/B154 °C
Linear coefficient of thermal expansionTDISO 11359-21.1E-04 cm/cm/°C