Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC GP1000ML-KA626 广州LG
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Thermal Properties
Test Condition
Test Method
Unit
PC/广州LG/GP1000ML-KA626
RTI
UL 746
°C
1
RTI Imp
UL 746
°C
1
RTI Elec
UL 746
°C
1
Vicat Softening Temperature
ASTM D15255
°C
1
Deflection Temperature Under Load?
1.8 MPa, 未退火, 6.40 mm, 注塑
ASTM D648
°C
1
Hardness
Test Condition
Test Method
Unit
PC/广州LG/GP1000ML-KA626
Rockwell Hardness
R 级, 23°C, 注塑
ASTM D785
1
Injection
Test Condition
Test Method
Unit
PC/广州LG/GP1000ML-KA626
Suggested Max Moisture
%
0
Middle Temperature
°C
2
Processing (Melt) Temp
°C
3
Drying Time
hr
3
Rear Temperature
°C
2
Nozzle Temperature
°C
3
Drying Temperature
°C
1
Front Temperature
°C
3
Back Pressure
Mpa
0
Mold Temperature
°C
8
Screw Speed
rpm
4
Physical
Test Condition
Test Method
Unit
PC/广州LG/GP1000ML-KA626
Melt Mass-Flow Rate
300°C/1.2 kg
ASTM D1238
g/10 min
1
Modeling Shrinkage - Flow
23°C, 3.20 mm, 注塑
ASTM D955
%
0
Mechanical Properties
Test Condition
Test Method
Unit
PC/广州LG/GP1000ML-KA626
Tensile Strength
屈服, 23°C, 3.20 mm, 注塑
ASTM D638
Mpa
6
Flexural Modulus
23°C, 3.20 mm, 注塑
ASTM D790
Mpa
2
Tensile Elongation
断裂, 23°C, 3.20 mm, 注塑
ASTM D638
%
1
Flexural Strength
23°C, 3.20 mm, 注塑
ASTM D790
Mpa
9
Flammability
Test Condition
Test Method
Unit
PC/广州LG/GP1000ML-KA626
UL flame retardant rating
3.2 mm
UL 94
H
UL flame retardant rating
1.5 mm
UL 94
H
Electrical Properties
Test Condition
Test Method
Unit
PC/广州LG/GP1000ML-KA626
Volume Resistivity
23°C
ASTM D257
ohms·cm
2
Comparative Tracking Index
IEC 60112
V
2