LCP E6007LHF-Z SUMITOMO JAPAN

SUMIKASUPER®

--

Low warpage,Good forming performance,enhance,Glass fiber reinforced

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

hardness	Test Condition	Test Method	SUMITOMO JAPAN/E6007LHF-Z
Rockwell hardness	R-Scale	ASTM D785	106

thermal performance	Test Condition	Test Method	SUMITOMO JAPAN/E6007LHF-Z
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	269 °C
Linear coefficient of thermal expansion	Across Flow : 150°C	Internal Method	8.5E-5 cm/cm/°C
Linear coefficient of thermal expansion		Flow : 150°C	Internal Method	2.0E-6 cm/cm/°C

mechanical properties	Test Condition	Test Method	SUMITOMO JAPAN/E6007LHF-Z
Bending modulus	23°C	ASTM D790	11800 Mpa
bending strength	23°C	ASTM D790	158 Mpa
elongation	Break	ASTM D638	5.1 %
tensile strength		ASTM D638	157 Mpa

Electrical performance	Test Condition	Test Method	SUMITOMO JAPAN/E6007LHF-Z
Arc resistance		ASTM D495	124 sec
Compared to the anti leakage trace index		IEC 60112	V
Dielectric constant	1.00 GHz	ASTM D150	3.50
Dielectric constant		1 MHz	ASTM D150	3.80
Dissipation factor	1 MHz	ASTM D150	0.026
Dissipation factor		1.00 GHz	ASTM D150	4.0E-3
Volume resistivity		ASTM D257	1.0E+15 ohms·cm

other	Test Condition	Test Method	SUMITOMO JAPAN/E6007LHF-Z
purpose			IT办公

Physical properties	Test Condition	Test Method	SUMITOMO JAPAN/E6007LHF-Z
Shrinkage rate	Flow	Internal Method	0.20 %
Shrinkage rate		横向Flow	Internal Method	0.60 %
Water absorption rate	Saturation	ASTM D570	0.020 %

impact performance	Test Condition	Test Method	SUMITOMO JAPAN/E6007LHF-Z
Suspended wall beam without notch impact strength	6.40 mm	ASTM D256	250 J/m

flammability	Test Condition	Test Method	SUMITOMO JAPAN/E6007LHF-Z
Extreme Oxygen Index		ISO 527-1	40 %
Solder resistance		Internal Method	300 °C
UL flame retardant rating	0.30 mm	UL 94	V-0

injection	Test Condition	Test Method	SUMITOMO JAPAN/E6007LHF-Z
Back pressure			1.00 to 5.00 Mpa
drying temperature			130 °C
drying time			4.0 to 24 hr
Injection pressure			80.0 to 160 Mpa
Injection speed			中等偏快
Maintain pressure			20.0 to 40.0 Mpa
Mold temperature			40 to 160 °C
Processing (melt) temperature			350 °C
Screw speed			50 to 100 rpm
Spray nozzle temperature			340 to 360 °C
Temperature at the front of the material cylinder			340 to 360 °C
Temperature at the rear of the barrel			280 to 320 °C
Temperature in the middle of the barrel			320 to 340 °C