Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS AC3100AF FCFC TAIWAN
TAIRILOY®
Electrical field,Electronic field,Automotive sector,Medical packaging
High mobility,Flame retardant,Antimony free,Bromine free,Self extinguishing
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | FCFC TAIWAN/AC3100AF |
|---|---|---|---|
| Rockwell hardness | R 计秤, 23°C | ISO 2039-2 | 116 |
| R 级, 23°C | ASTM D785 | 116 |
| Mechanical properties | Test Condition | Test Method | FCFC TAIWAN/AC3100AF |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 95.0 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 2350 Mpa |
| tensile strength | 23°C | ASTM D638 | 57.0 Mpa |
| flammability | Test Condition | Test Method | FCFC TAIWAN/AC3100AF |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | FCFC TAIWAN/AC3100AF |
|---|---|---|---|
| Shrinkage rate | 流动 : 3.20 mm | ASTM D955 | 0.40 - 0.60 % |
| melt mass-flow rate | 240°C/5.0 kg | ASTM D1238 | 50 g/10 min |
| Shrinkage rate | 3.20 mm | ISO 2577 | 0.40 - 0.60 % |
| Thermal performance | Test Condition | Test Method | FCFC TAIWAN/AC3100AF |
|---|---|---|---|
| Heat distortion temperature | 1.8 MPa, 未退火, 6.35 mm，HDT | ASTM D648 | 88.0 °C |
| injection | Test Condition | Test Method | FCFC TAIWAN/AC3100AF |
|---|---|---|---|
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 220 to 250 °C | ||
| Temperature at the rear of the barrel | 200 to 230 °C | ||
| Processing (melt) temperature | 230 to 260 °C | ||
| Hopper temperature | 60 to 80 °C | ||
| drying temperature | 80 to 90 °C | ||
| Temperature at the front of the material cylinder | 230 to 260 °C | ||
| Back pressure | 0.345 to 0.689 Mpa | ||
| Temperature | 50 to 70 °C | ||
| Spray nozzle temperature | 220 to 250 °C |