Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 1502S ASAHI JAPAN
Leona™
Automotive Applications,Gears
high strength,High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/1502S |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | NoBreak |
| hardness | Test Condition | Test Method | ASAHI JAPAN/1502S |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 80 |
| R计秤 | ISO 2039-2 | 120 | |
| M计秤 | ISO 2039-2 | 80 | |
| R计秤 | ASTM D785 | 120 |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/1502S |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 20 KV/mm | |
| Surface Resistivity | ASTM D257 | 1E+14 ohms | |
| Volume resistivity | 23°C | IEC 60093 | 1E+15 ohms·cm |
| dielectric strength | ASTM D149 | 20 KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | V |
| Surface Resistivity | IEC 60093 | 1E+14 ohms |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/1502S |
|---|---|---|---|
| Taber abraser | 1000Cycles | ASTM D1044 | -- mg |
| elongation | 断裂 | ASTM D638 | 80 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | -- % |
| bending strength | 23°C | ISO 178 | 110 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 84.0 Mpa |
| bending strength | ASTM D790 | 118 Mpa | |
| Tensile strain | 屈服,23°C | ISO 527-2 | 4.5 % |
| Flexural modulus | 23°C | ISO 178 | 2700 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 2900 Mpa |
| Flexural modulus | ASTM D790 | 2800 Mpa | |
| tensile strength | ASTM D638 | 79.0 Mpa |
| physical property | Test Condition | Test Method | ASAHI JAPAN/1502S |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.3-2.0 % |
| Water absorption rate | 饱和,23°C | -- % | |
| 平衡,23°C,50%RH | ISO 62 | -- % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/1502S |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 70.0 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 230 °C | |
| thermal conductivity | 0.20 W/m/K | ||
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 195 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 65.0 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 8E-05 cm/cm/°C |
| specific heat | 1670 J/kg/°C |