Impact resistance	Test Condition	Test Method	DSM HOLAND/OCD2100-BK27021
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	90 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	65 kJ/m²

Mechanical properties	Test Condition	Test Method	DSM HOLAND/OCD2100-BK27021
tensile strength	断裂, 160°C	ISO 527-2	85.0 Mpa
Tensile modulus	--	ISO 527-2	13000 Mpa
tensile strength	断裂, 180°C	ISO 527-2	75.0 Mpa
Tensile strain	断裂, 120°C	ISO 527-2	10 %
tensile strength	断裂	ISO 527-2	210 Mpa
Flexural modulus	--	ISO 178	13000 Mpa
Tensile modulus	180°C	ISO 527-2	4200 Mpa
tensile strength	断裂, 120°C	ISO 527-2	100 Mpa
Tensile modulus	160°C	ISO 527-2	4600 Mpa
Tensile modulus		120°C	ISO 527-2	5000 Mpa
Tensile strain	断裂, 200°C	ISO 527-2	13 %
Flexural modulus	160°C	ISO 178	4600 Mpa
Flexural modulus		180°C	ISO 178	4200 Mpa
Tensile strain	断裂, 180°C	ISO 527-2	12 %
Tensile strain		断裂	ISO 527-2	3.0 %
Flexural modulus	200°C	ISO 178	3400 Mpa
Tensile strain	断裂, 160°C	ISO 527-2	11 %
Tensile modulus	200°C	ISO 527-2	3400 Mpa
Flexural modulus	120°C	ISO 178	5000 Mpa
tensile strength	断裂, 200°C	ISO 527-2	60.0 Mpa

Electrical performance	Test Condition	Test Method	DSM HOLAND/OCD2100-BK27021
Compared to the Leakage Tracking Index (CTI)		IEC 60112	V

physical property	Test Condition	Test Method	DSM HOLAND/OCD2100-BK27021
Water absorption rate	平衡, 23°C, 50% RH	ISO 62	2.2 %
Shrinkage rate	流量	ISO 294-4	0.50 %
Shrinkage rate		横向流量	ISO 294-4	1.0 %

Thermal performance	Test Condition	Test Method	DSM HOLAND/OCD2100-BK27021
melting temperature		ISO 11357-3	282 °C
Heat distortion temperature	0.45 MPa, 未退火，HDT	ISO 75-2/B	270 °C
Heat distortion temperature		1.8 MPa, 未退火，HDT	ISO 75-2/A	256 °C
Linear coefficient of thermal expansion	流动	ISO 11359-2	2.5E-5 cm/cm/°C
Linear coefficient of thermal expansion		横向	ISO 11359-2	5.0E-5 cm/cm/°C