PC Lupoy® 1603-06 LG Chem Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG Chem Ltd./Lupoy® 1603-06 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 890 J/m |
| 23°C | ASTM D256 | NoBreak |
| Mechanical properties | Test Condition | Test Method | LG Chem Ltd./Lupoy® 1603-06 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 90 % |
| 屈服 | ASTM D638 | 6.0 % | |
| Tensile modulus | ASTM D638 | 2300 MPa | |
| tensile strength | 断裂 | ASTM D638 | 56.0 MPa |
| Flexural modulus | ASTM D790 | 2300 MPa | |
| tensile strength | 屈服 | ASTM D638 | 60.0 MPa |
| bending strength | ASTM D790 | 96.0 MPa |
| optical performance | Test Condition | Test Method | LG Chem Ltd./Lupoy® 1603-06 |
|---|---|---|---|
| transmissivity | ASTM D1003 | 89.0 % | |
| refractive index | ASTM D542 | 1.586 | |
| Haze ratio | ASTM D1003 | 0.70to1.5 % |
| physical property | Test Condition | Test Method | LG Chem Ltd./Lupoy® 1603-06 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.50to0.70 % |
| Water absorption rate | 平衡,23°C,50%RH | ASTM D570 | 0.32 % |
| 23°C,24hr | ASTM D570 | 0.15 % | |
| density | ASTM D792 | 1.20 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 6.0 g/10min |
| Thermal performance | Test Condition | Test Method | LG Chem Ltd./Lupoy® 1603-06 |
|---|---|---|---|
| vicat | ASTM D15253 | 150 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ASTM D648 | 126 °C |
| Linear coefficient of thermal expansion | MD：-40到82°C | ASTM D696 | 6.8E-05 cm/cm/°C |