Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO GFN1520V-801F SABIC INNOVATIVE SHANGHAI
FLEX NORYL™
Automotive components、Laptop case
High temperature resistan、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/GFN1520V-801F
Melt Volume-Flow Rate (MVR)
300°C/5.0kg
ISO1133
cm3/10min
1
Melt mass flow rate
300°C/5.0kg
ASTMD1238
g/10min
1
Shrinkage rate
MD：3.20mm
内部方法
%
0
Water absorption rate
24hr
ASTMD570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/GFN1520V-801F
Simple supported beam without notch impact strength
-30°C
ISO179/1eU
kJ/m²
3
Simple supported beam without notch impact strength
23°C
ISO179/1eU
kJ/m²
3
Tensile modulus
ASTMD638
Mpa
4
Tensile modulus
ISO527-2/1
Mpa
4
tensile strength
断裂
ASTMD638
Mpa
6
tensile strength
断裂
ISO527-2
Mpa
6
elongation
断裂
ASTMD638
%
3
elongation
断裂
ISO527-2
%
3
Bending modulus
50.0mm跨距4
ASTMD790
Mpa
3
Bending modulus
100mmSpan5
ASTMD790
Mpa
3
Bending modulus
ISO178
Mpa
4
bending strength
ISO178
Mpa
1
bending strength
屈服,50.0mm跨距4
ASTMD790
Mpa
1
bending strength
Yield,100mmSpan5
ASTMD790
Mpa
1
Unscented Izod Impact Strength
-30°C
ISO180/1U
kJ/m²
2
Unscented Izod Impact Strength
23°C
ISO180/1U
kJ/m²
2
Suspended wall beam gap impact strength
-30°C
ISO180/1A
kJ/m²
9
Suspended wall beam gap impact strength
23°C
ISO180/1A
kJ/m²
1
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
2
Thermal performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/GFN1520V-801F
RTI Imp
UL746
°C
9
RTIElec
UL746
°C
9
RTIStr
UL746
°C
9
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
0.45MPa,Unannealed,100mmSpan
ISO75-2/Be
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,Unannealed,100mmSpan
ISO75-2/Ae
°C
1
vicat softening point
--
ISO306/B50
°C
1
vicat softening point
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
5
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
7