PA4T K11 BK DSM HOLAND
ForTii®
Electronic and electrical、Automotive Applications
Thermal stability、Lubricity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DSM HOLAND/K11 BK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 55 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DSM HOLAND/K11 BK |
|---|---|---|---|
| tensile strength | 断裂, 160°C | ISO 527-2 | 90.0 Mpa |
| Tensile modulus | -- | ISO 527-2 | 11000 Mpa |
| Tensile strain | 断裂, 120°C | ISO 527-2 | 2.8 % |
| tensile strength | 断裂 | ISO 527-2 | 180 Mpa |
| Flexural modulus | -- | ISO 178 | 10000 Mpa |
| tensile strength | 断裂, 120°C | ISO 527-2 | 130 Mpa |
| Tensile modulus | 160°C | ISO 527-2 | 5000 Mpa |
| 120°C | ISO 527-2 | 8000 Mpa | |
| Tensile strain | 断裂, 200°C | ISO 527-2 | 5.8 % |
| Flexural modulus | 160°C | ISO 178 | 5000 Mpa |
| bending strength | ISO 178 | 290 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.0 % |
| Flexural modulus | 200°C | ISO 178 | 4000 Mpa |
| Tensile strain | 断裂, 160°C | ISO 527-2 | 4.6 % |
| Tensile modulus | 200°C | ISO 527-2 | 5000 Mpa |
| tensile strength | 断裂, 200°C | ISO 527-2 | 75.0 Mpa |
| Electrical performance | Test Condition | Test Method | DSM HOLAND/K11 BK |
|---|---|---|---|
| relative permittivity | 100 Hz | IEC 60250 | 5.00 |
| dielectric strength | IEC 60243-1 | 33 KV/mm | |
| Volume resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| relative permittivity | 1.00 GHz | IEC 60250 | 3.90 |
| 1 MHz | IEC 60250 | 4.50 | |
| 10.0 GHz | IEC 60250 | 3.80 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| flammability | Test Condition | Test Method | DSM HOLAND/K11 BK |
|---|---|---|---|
| Flammability level | UL 94 | HB |
| physical property | Test Condition | Test Method | DSM HOLAND/K11 BK |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 2.1 % |
| Shrinkage rate | 流量 | ISO 294-4 | 0.40 % |
| 横向流量 | ISO 294-4 | 1.3 % |
| Thermal performance | Test Condition | Test Method | DSM HOLAND/K11 BK |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 325 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 305 °C |
| Thermal Index - 5000 hr | IEC 60216 | 174 °C | |
| Linear coefficient of thermal expansion | 流动 | ASTM D696 | 3.0E-5 cm/cm/°C |
| 横向 | ASTM D696 | 5.0E-5 cm/cm/°C |