Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS C1200HF-BL1D302 SABIC INNOVATIVE NANSHA
CYCOLOY™ Resin
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C1200HF-BL1D302 |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 54.2 J |
| -30°C,TotalEnergy | ASTM D3763 | 54.2 J | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 34 kJ/m² |
| 23°C | ISO 180/1A | 49 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C1200HF-BL1D302 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2370 Mpa | |
| ASTM D638 | 2280 Mpa | ||
| tensile strength | 屈服 | ISO 527-2/50 | 55.0 Mpa |
| elongation | 断裂 | ASTM D638 | 150 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 88.3 Mpa |
| elongation | 屈服 | ASTM D638 | 5.0 % |
| bending strength | ISO 178 | 86.0 Mpa | |
| Flexural modulus | ISO 178 | 2250 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 57.2 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 110 % |
| 屈服 | ISO 527-2/50 | 4.8 % | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2340 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C1200HF-BL1D302 |
|---|---|---|---|
| High arc combustion index (HAI) | HAI | UL 746 | PLC 1 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C1200HF-BL1D302 |
|---|---|---|---|
| UL flame retardant rating | 1.2mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C1200HF-BL1D302 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 19 g/10min |
| Melt volume flow rate | 265°C/5.0kg | ISO 1133 | 24.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/C1200HF-BL1D302 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 130 °C |
| vicat | ISO 306/B50 | 130 °C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 129 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C |
| RTI Imp | UL 746 | 80.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 110 °C |
| RTI Str | UL 746 | 105 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 113 °C |
| RTI Elec | UL 746 | 105 °C |